ABS POLYLAC® PA-777C CHI MEI CORPORATION
--
--
--
--
--
--
--
--
--
--
--
--
--
--
--
--
--
--
Plastic Datasheets
Impact resistance | Test Condition | Test Method | CHI MEI CORPORATION/POLYLAC® PA-777C |
---|---|---|---|
Dart impact | 23°C | ASTM D4226 | 17.0 J/cm |
Impact strength of cantilever beam gap | -30°C | ISO 180/1A | 9.0 kJ/m² |
Dart impact | -30°C | ASTM D4226 | 9.00 J/cm |
Impact strength of cantilever beam gap | 23°C | ISO 180/1A | 18 kJ/m² |
Mechanical properties | Test Condition | Test Method | CHI MEI CORPORATION/POLYLAC® PA-777C |
---|---|---|---|
Flexural modulus | ISO 178 | 2200 MPa | |
Tensile strain | 断裂 | ISO 527-2/50 | 44 % |
tensile strength | 屈服 | ISO 527-2/50 | 44.0 MPa |
bending strength | ISO 178 | 69.0 MPa | |
tensile strength | 断裂 | ISO 527-2/50 | 35.0 MPa |
flammability | Test Condition | Test Method | CHI MEI CORPORATION/POLYLAC® PA-777C |
---|---|---|---|
UL flame retardant rating | 1.5mm | UL 94 | HB |
physical property | Test Condition | Test Method | CHI MEI CORPORATION/POLYLAC® PA-777C |
---|---|---|---|
density | 23°C | ISO 1183 | 1.06 g/cm³ |
Shrinkage rate | ISO 294-4 | 0.30to0.60 % | |
melt mass-flow rate | 220°C/10.0kg | ISO 1133 | 7.0 g/10min |
Thermal performance | Test Condition | Test Method | CHI MEI CORPORATION/POLYLAC® PA-777C |
---|---|---|---|
vicat | -- | ISO 306/A50 | 119 °C |
Heat distortion temperature | 1.8MPa,退火,HDT | ISO 75-2/A | 112 °C |
1.8MPa,未退火,HDT | ISO 75-2/A | 92.0 °C | |
vicat | -- | ISO 306/B50 | 112 °C |
Linear coefficient of thermal expansion | MD | ISO 11359-2 | 8.2E-05 cm/cm/°C |