PAI

PAI 4310 USA Suwei

Properties:
Adding ingredients such as graphite powder fluorinated polymer a composite with high compressive strength versatility high performance low friction coefficient and wear resistance
Usages:
Bearings thrust washers wear pads slats piston rings seals blades and valve seats
Compare

Technical Data Sheet

Basic Performance	Test Condition	Test Method	Test Result
Water absorption rate	24hr	ASTM D570	0.28 %
density		ASTM D792	1.47 g/cm3

mechanical properties	Test Condition	Test Method	Test Result
Poisson's ratio			0.39
Impact strength of cantilever beam gap	Unnotched 3.2mm	ASTM D256	404 J/m
Impact strength of cantilever beam gap	Impact strength of cantilever beam gap	（Notched）3.2mm	ASTM D256	64 J/m
shear strength	23℃	ASTM D732	112 MPa
Compressive modulus		ASTM D695	5.3 MPa
compressive strength		ASTM D695	166 MPa
Bending modulus	23℃	ASTM D790	6900 MPa
bending strength	23℃	ASTM D790	215 MPa
Tensile modulus	23℃	ASTM D790	6600 MPa
Elongation at Break	23℃	ASTM D1708	7 %
tensile strength	23℃	ASTM D1708	163 MPa

thermal performance	Test Condition	Test Method	Test Result
Hot deformation temperature	1.8MPa	ASTM D648	279 ℃
Linear coefficient of thermal expansion		ASTM D696	25.2 ppm/°C
Extreme Oxygen Index		ASTM D2863	44 %
UL flame retardant rating		UL 94	V-0

IMPORTANT NOTES: Plas.com collected the data in the data sheet from the material manufacturers. Plas.com makes the best effort to improve the accuracy of the data, but has no responsibility for the data. We strongly recommend verifying the validity of the data with the material manufacturers before making a final decision.