Technical Data Sheet
| physical property | Test Condition | Test Method | Test Result |
|---|
| density | | ASTM D792 | 1.30 g/cm³ |
| Shrinkage rate | | ASTM D955 | 1.0 % |
| Water absorption rate | | ASTM D570 | 0.15 % |
| hardness | Test Condition | Test Method | Test Result |
|---|
| Rockwell hardness | M-Scale | ASTM D785 | 95 |
| Mechanical properties | Test Condition | Test Method | Test Result |
|---|
| Tensile modulus | | ASTM D638 | 4100 MPa |
| tensile strength | | ASTM D638 | 110 MPa |
| elongation | Break | ASTM D638 | 30 % |
| Flexural modulus | | ASTM D790 | 4100 MPa |
| bending strength | | ASTM D790 | 172 MPa |
| Impact resistance | Test Condition | Test Method | Test Result |
|---|
| Impact strength of cantilever beam gap | | ASTM D256 | 4.0 J/m |
| Electrical performance | Test Condition | Test Method | Test Result |
|---|
| Surface Resistivity | | ASTM D257 | 5.1 ohms |
| Volume resistivity | | ASTM D257 | 2.5 ohms·cm |
| dielectric strength | | ASTM D149 | 240 kV/mm |
| dielectric constant | | ASTM D150 | 3.30 |
| Dissipation Factor | | ASTM D150 | 4E-03 |
| Thermal performance | Test Condition | Test Method | Test Result |
|---|
| melting temperature | | DSC | 360 °C |
| Linear coefficient of thermal expansion | | ASTM D696 | 3.6E-05 cm/cm/°C |
| thermal conductivity | | ASTMC177 | 0.25 W/m/K |
| Glass Transition Temperature | | ASTME1356 | 177 °C |
| Heat distortion temperature | | ASTM D648 | 191 °C |
IMPORTANT NOTES: Plas.com collected the data in the data sheet from the material manufacturers. Plas.com makes the best effort to improve the accuracy of the data, but has no responsibility for the data. We strongly recommend verifying the validity of the data with the material manufacturers before making a final decision.