| physical property | Test Condition | Test Method | Test Result |
|---|
| Shrinkage rate | | 内部方法 | 0.60to0.90 % |
| Shrinkage rate | | 内部方法 | 0.35to0.60 % |
| Water absorption rate | | ISO 62 | 0.050 % |
| Water absorption rate | | ISO 62 | 0.25 % |
| density | | ISO 1183 | 1.33 g/cm³ |
| melt mass-flow rate | | ISO 1133 | 10 g/10min |
| flammability | Test Condition | Test Method | Test Result |
|---|
| UL flame retardant rating | | UL 94 | HB |
| Burning wire flammability index | | IEC 60695-2-12 | 650 °C |
| Limiting Oxygen Index | | ASTM D2863 | 20 % |
| Supplementary Information | Test Condition | Test Method | Test Result |
|---|
| ReinforcementContent | | ISO 3451 | 15 % |
| Mechanical properties | Test Condition | Test Method | Test Result |
|---|
| Tensile modulus | | ISO 527-2/1 | 5000 MPa |
| tensile strength | Break | ISO 527-2/50 | 85.0 MPa |
| Tensile strain | Break | ISO 527-2/50 | 3.0 % |
| Flexural modulus | | ISO 178 | 4100 MPa |
| bending strength | | ISO 178 | 115 MPa |
| Impact resistance | Test Condition | Test Method | Test Result |
|---|
| Charpy Notched Impact Strength | | ISO 179/1eA | 5.1 kJ/m² |
| Impact strength of cantilever beam gap | | ASTM D256 | 62 J/m |
| Electrical performance | Test Condition | Test Method | Test Result |
|---|
| Compared to the Leakage Tracking Index (CTI) | | IEC 60112 | PLC 1 |
| Thermal performance | Test Condition | Test Method | Test Result |
|---|
| Heat distortion temperature | | ISO 75-2/A | 165 °C |
| vicat | | ISO 306/B50 | 175 °C |
| melting temperature | | ISO 11357-3 | 220 °C |
IMPORTANT NOTES: Plas.com collected the data in the data sheet from the material manufacturers. Plas.com makes the best effort to improve the accuracy of the data, but has no responsibility for the data. We strongly recommend verifying the validity of the data with the material manufacturers before making a final decision.