Technical Data Sheet
| physical property | Test Condition | Test Method | Test Result |
|---|
| Disassembly rate | | | 1.569 |
| Shrinkage rate | | | 0.3-0.7 % |
| Melting temperature range for pipeline extrusion | | | 220-240 °C |
| Water absorption | | | 0.2 % |
| melt mass-flow rate | | | 12 |
| melt mass-flow rate | | | 10 |
| Melting temperature range for injection molding | | | 220-270 °C |
| Temperature range of mold | | | 40-80 °C |
| other | Test Condition | Test Method | Test Result |
|---|
| | | 通用级别 |
| purpose | | | 制笔 浴室器具 化妆品容器 盛具 牙刷手柄 拨号盘 |
| Mechanical properties | Test Condition | Test Method | Test Result |
|---|
| Rockwell hardness | | ASTM D785 | 83 |
| Charpy Notched Impact Strength | | | 2 KJ/m |
| Rockwell hardness | | | 83 M |
| Impact strength of cantilever beam gap | | | 2 KJ/m |
| | | 165 Mpa |
| Breaking stress | | | 75 Mpa |
| Yield stress under maximum stress | | | 125 Mpa |
| elongation | | | 3 % |
| Tensile modulus of elasticity | | | 3800 Mpa |
| Charpy impact strength | | | 18/18 KJ/m |
| Tensile creep modulus | | | 2800 Mpa |
| Physical properties | Test Condition | Test Method | Test Result |
|---|
| density | | ASTM D792/ISO 1183 | 10.8 kg·cm/cm(J/M)ft·lb/in |
| Mold Shrinkage | | ASTM D955 | 0.3-0.7 % |
| melt mass-flow rate | | ASTM D1238/ISO 1133 | 12 g/10min |
| melt mass-flow rate | | ASTM D1238/ISO 1133 | 10 g/10min |
| Water absorption rate | | ASTM D570/ISO 62 | 0.2 % |
| Electrical performance | Test Condition | Test Method | Test Result |
|---|
| | | CTI 425 |
| dielectric constant | | | 3/2.7 |
| | | 10 Ω.cm |
| Surface Resistivity | | | 10 Ω |
| | | CTI 200M |
| dielectric strength | | | 95 KV/mm |
| loss angle | | | 0.004/0.007 |
| Thermal performance | Test Condition | Test Method | Test Result |
|---|
| melting point | | | 85 ℃（℉） |
| vicat | | ASTM D1525/ISO R306 | 106 ℃（℉） |
| Linear expansion coefficient | | ASTM D696/ISO 11359 | 7 mm/mm.℃ |
| | | 102 °C |
| Maximum operating temperature | | | 85 °C |
| | | 98 °C |
| Conductivity | | | 0.17 W/K.m |
| Linear expansion coefficient | | | 7 |
| vicat | | | 106 °C |
IMPORTANT NOTES: Plas.com collected the data in the data sheet from the material manufacturers. Plas.com makes the best effort to improve the accuracy of the data, but has no responsibility for the data. We strongly recommend verifying the validity of the data with the material manufacturers before making a final decision.