Material Comparison
Product Info
Product Name
Brand Name
Usages
Properties
Certificates
AS(SAN) 368R BASF GERMANY
Luran®
toothbrush、Household daily necessiti、Monitor、electrical equipment
transparent、stability
UL
--
--
--
--
--
--
--
--
--
--
--
--
--
--
--
Plastic Datasheets
| Mechanical properties | Test Condition | Test Method | BASF GERMANY/368R |
|---|---|---|---|
| elongation | 3 % | ||
| Rockwell hardness | 83 M | ||
| Charpy impact strength | +23/-40℃ | 18/18 KJ/m | |
| Ball Indentation Hardness | 165 Mpa | ||
| Yield stress under maximum stress | 125 Mpa | ||
| Impact strength of cantilever beam gap | 23℃ | 2 KJ/m | |
| Breaking stress | 75 Mpa | ||
| Rockwell hardness | ASTM D785 | 83 | |
| Charpy Notched Impact Strength | 23℃ | 2 KJ/m | |
| Tensile creep modulus | 1000h 伸长率＜＝0.5%+23℃ | 2800 Mpa | |
| Tensile modulus of elasticity | 3800 Mpa |
| Electrical performance | Test Condition | Test Method | BASF GERMANY/368R |
|---|---|---|---|
| Comparative Tracking Index | 试验溶液A/CTIM | CTI 425 | |
| Surface Resistivity | 10 Ω | ||
| loss angle | 100Hz/1MHz | 0.004/0.007 | |
| Volume Resistivity | 10 Ω.cm | ||
| Comparative Tracking Index | 试验溶液B | CTI 200M | |
| dielectric strength | K20/P20 | 95 KV/mm | |
| dielectric constant | 100Hz/1MHz | 3/2.7 |
| other | Test Condition | Test Method | BASF GERMANY/368R |
|---|---|---|---|
| characteristic | 通用级别 | ||
| purpose | 制笔 浴室器具 化妆品容器 盛具 牙刷手柄 拨号盘 |
| Physical properties | Test Condition | Test Method | BASF GERMANY/368R |
|---|---|---|---|
| melt mass-flow rate | ASTM D1238/ISO 1133 | 10 g/10min | |
| Mold Shrinkage | ASTM D955 | 0.3-0.7 % | |
| density | ASTM D792/ISO 1183 | 10.8 kg·cm/cm(J/M)ft·lb/in | |
| Water absorption rate | ASTM D570/ISO 62 | 0.2 % |
| physical property | Test Condition | Test Method | BASF GERMANY/368R |
|---|---|---|---|
| melt mass-flow rate | 200/21 6 | 12 | |
| Water absorption | 0.2 % | ||
| Melting temperature range for pipeline extrusion | 220-240 °C | ||
| Melting temperature range for injection molding | 220-270 °C | ||
| Disassembly rate | 1.569 | ||
| Shrinkage rate | 0.3-0.7 % | ||
| melt mass-flow rate | 220/10 | 10 | |
| Temperature range of mold | 40-80 °C |
| Thermal performance | Test Condition | Test Method | BASF GERMANY/368R |
|---|---|---|---|
| Heat Deflection Temperature | 1.8MPa(HDT A) | 98 °C | |
| vicat | ASTM D1525/ISO R306 | 106 ℃（℉） | |
| Heat Deflection Temperature | 0.45MPa(HDT B) | 102 °C | |
| Conductivity | 0.17 W/K.m | ||
| Linear expansion coefficient | 纵向(23-80)℃ | 7 | |
| vicat | 106 °C | ||
| melting point | 85 ℃（℉） | ||
| Maximum operating temperature | 85 °C | ||
| Linear expansion coefficient | ASTM D696/ISO 11359 | 7 mm/mm.℃ |