| physical property | Test Condition | Test Method | Test Result |
|---|
| density | | ISO 1183 | 1.42 g/cm³ |
| Shrinkage rate | | | 0.90 % |
| Shrinkage rate | | | 0.10 % |
| Water absorption rate | | ISO 62 | 0.50 % |
| hardness | Test Condition | Test Method | Test Result |
|---|
| Rockwell hardness | M-Scale | ASTM D785 | 105 |
| Mechanical properties | Test Condition | Test Method | Test Result |
|---|
| Tensile modulus | | ISO 527-2 | 15000 MPa |
| tensile strength | Yield | ISO 527-2 | 155 MPa |
| tensile strength | | ISO 527-2 | 98.0 MPa |
| Tensile strain | Break | ISO 527-2 | 2.0 % |
| Tensile strain | | ISO 527-2 | 2.8 % |
| Flexural modulus | | ISO 178 | 12500 MPa |
| Flexural modulus | | ISO 178 | 6400 MPa |
| bending strength | | ISO 178 | 230 MPa |
| bending strength | | ISO 178 | 164 MPa |
| Compression Modulus | | ISO 604 | 12000 MPa |
| compression stress | | ISO 604 | 200 MPa |
| shear modulus | | ISO 15310 | 2200 MPa |
| shear strength | | ASTM D732 | 94.0 MPa |
| Poisson's ratio | | ASTME132 | 0.41 |
| Impact resistance | Test Condition | Test Method | Test Result |
|---|
| Suspended wall beam without notch impact strength | | ISO 180 | 30 kJ/m² |
| Impact strength of cantilever beam gap | | ISO 180 | 5.5 kJ/m² |
| Filling analysis | Test Condition | Test Method | Test Result |
|---|
| MeltViscosity | | 内部方法 | 0.370 kPa |
| Thermal performance | Test Condition | Test Method | Test Result |
|---|
| melting temperature | | | 343 °C |
| Linear coefficient of thermal expansion | | ASTM D696 | 1.2E-05 cm/cm/°C |
| Linear coefficient of thermal expansion | | ASTM D696 | 1.5E-05 cm/cm/°C |
IMPORTANT NOTES: Plas.com collected the data in the data sheet from the material manufacturers. Plas.com makes the best effort to improve the accuracy of the data, but has no responsibility for the data. We strongly recommend verifying the validity of the data with the material manufacturers before making a final decision.