Material Comparison
Product Info
Product Name
Brand Name
Usages
Properties
Certificates
PEEK MOTIS™ LV Invibio Inc.
--
--
--
--
--
--
--
--
--
--
--
--
--
--
--
--
--
--
Plastic Datasheets
| Impact resistance | Test Condition | Test Method | Invibio Inc./MOTIS™ LV |
|---|---|---|---|
| Impact strength of cantilever beam gap | ISO 180 | 5.5 kJ/m² | |
| Suspended wall beam without notch impact strength | ISO 180 | 30 kJ/m² |
| hardness | Test Condition | Test Method | Invibio Inc./MOTIS™ LV |
|---|---|---|---|
| Rockwell hardness | M级 | ASTM D785 | 105 |
| Mechanical properties | Test Condition | Test Method | Invibio Inc./MOTIS™ LV |
|---|---|---|---|
| Compression Modulus | ISO 604 | 12000 MPa | |
| Tensile modulus | ISO 527-2 | 15000 MPa | |
| shear modulus | ISO 15310 | 2200 MPa | |
| tensile strength | 屈服 | ISO 527-2 | 155 MPa |
| Tensile strain | 断裂2 | ISO 527-2 | 2.8 % |
| Poisson's ratio | ASTME132 | 0.41 | |
| bending strength | --2 | ISO 178 | 164 MPa |
| Tensile strain | 断裂 | ISO 527-2 | 2.0 % |
| compression stress | ISO 604 | 200 MPa | |
| Flexural modulus | -- | ISO 178 | 12500 MPa |
| --2 | ISO 178 | 6400 MPa | |
| bending strength | -- | ISO 178 | 230 MPa |
| tensile strength | 屈服2 | ISO 527-2 | 98.0 MPa |
| shear strength | ASTM D732 | 94.0 MPa |
| Filling analysis | Test Condition | Test Method | Invibio Inc./MOTIS™ LV |
|---|---|---|---|
| MeltViscosity | 内部方法 | 0.370 kPa |
| physical property | Test Condition | Test Method | Invibio Inc./MOTIS™ LV |
|---|---|---|---|
| Water absorption rate | 23°C,24hr | ISO 62 | 0.50 % |
| Shrinkage rate | TD:210°C | 0.90 % | |
| density | ISO 1183 | 1.42 g/cm³ | |
| Shrinkage rate | MD:210°C | 0.10 % |
| Thermal performance | Test Condition | Test Method | Invibio Inc./MOTIS™ LV |
|---|---|---|---|
| melting temperature | 343 °C | ||
| Linear coefficient of thermal expansion | MD：--3 | ASTM D696 | 1.2E-05 cm/cm/°C |
| MD：--4 | ASTM D696 | 1.5E-05 cm/cm/°C |