PA12/PTFE LNP™ LUBRICOMP™ SP003
93
- Properties:lubricationwear resistant
- Usages:Electrical appliancesPlastic bag
Compare
View PricesTechnical Data Sheet
| physical property | Test Condition | Test Method | Test Result |
|---|---|---|---|
| Shrinkage rate | ASTMD955 | 0.90to1.1 % | |
| ASTMD955 | 1.8to2.0 % | ||
| ISO294-4 | 1.9 % | ||
| ISO294-4 | 1.0 % | ||
| Water absorption rate | ASTMD570 | 0.20 % |
| Mechanical properties | Test Condition | Test Method | Test Result |
|---|---|---|---|
| Tensile stress | ISO527-2 | 38.0 Mpa | |
| tensile strength | ASTMD638 | 35.2 Mpa | |
| Tensile stress | ISO527-2 | 36.0 Mpa | |
| elongation | ASTMD638 | 18 % | |
| Tensile strain | ISO527-2 | 18 % | |
| elongation | ASTMD638 | 24 % | |
| Tensile strain | ISO527-2 | 33 % | |
| Flexural modulus | ASTMD790 | 1380 Mpa | |
| ISO178 | 1300 Mpa | ||
| Bending stress | ISO178 | 44.0 Mpa | |
| Tensile modulus | ASTMD638 | 1380 Mpa | |
| ISO527-2/1 | 1580 Mpa | ||
| tensile strength | ASTMD638 | 37.9 Mpa | |
| ASTMD3702Modified | 0.23 | ||
| ASTMD3702Modified | 0.14 | ||
| Wear factor - Washer | ASTMD3702Modified | 13.5 10^-10in^5-min/ft-lb-hr |
| Impact resistance | Test Condition | Test Method | Test Result |
|---|---|---|---|
| Suspended wall beam gap impact strength 3 | ISO180/1A | 4.6 kJ/m² | |
| UnnotchedIzodImpactStrength3 | ISO180/1U | 48 kJ/m² | |
| Dart impact equipped with measuring instruments | ASTMD3763 | 5.00 J | |
| Multi axis Instrumented Impact Energy | ISO6603-2 | 7.80 J |
| Thermal performance | Test Condition | Test Method | Test Result |
|---|---|---|---|
| Hot deformation temperature 4 | ISO75-2/Bf | 134 °C | |
| ASTMD648 | 146 °C | ||
| Hot deformation temperature 4 | ISO75-2/Af | 147 °C | |
| ASTME831 | 1.1E-04 cm/cm/°C | ||
| ISO11359-2 | 1.1E-04 cm/cm/°C | ||
| ASTME831 | 1.1E-04 cm/cm/°C | ||
| ISO11359-2 | 1.1E-04 cm/cm/°C | ||
| ASTMD648 | 150 °C |
IMPORTANT NOTES: Plas.com collected the data in the data sheet from the material manufacturers. Plas.com makes the best effort to improve the accuracy of the data, but has no responsibility for the data. We strongly recommend verifying the validity of the data with the material manufacturers before making a final decision.