Material Comparison
Product Info
Product Name
Brand Name
Usages
Properties
Certificates
PA12/PTFE SP003 SABIC INNOVATIVE US
LNP™ LUBRICOMP™
Electrical appliances、Plastic bag
lubrication、wear resistant
--
--
--
--
--
--
--
--
--
--
--
--
--
--
--
Plastic Datasheets
| Impact resistance | Test Condition | Test Method | SABIC INNOVATIVE US/SP003 |
|---|---|---|---|
| Suspended wall beam gap impact strength 3 | 23°C | ISO180/1A | 4.6 kJ/m² |
| UnnotchedIzodImpactStrength3 | 23°C | ISO180/1U | 48 kJ/m² |
| Multi axis Instrumented Impact Energy | ISO6603-2 | 7.80 J | |
| Dart impact equipped with measuring instruments | 23°C,EnergyatPeakLoad | ASTMD3763 | 5.00 J |
| Mechanical properties | Test Condition | Test Method | SABIC INNOVATIVE US/SP003 |
|---|---|---|---|
| elongation | 断裂 | ASTMD638 | 24 % |
| Flexural modulus | ASTMD790 | 1380 Mpa | |
| Tensile stress | 屈服 | ISO527-2 | 38.0 Mpa |
| Bending stress | ISO178 | 44.0 Mpa | |
| Dynamic | ASTMD3702Modified | 0.23 | |
| Tensile modulus | ASTMD638 | 1380 Mpa | |
| Tensile strain | 断裂 | ISO527-2 | 33 % |
| Static | ASTMD3702Modified | 0.14 | |
| Tensile stress | 断裂 | ISO527-2 | 36.0 Mpa |
| elongation | 屈服 | ASTMD638 | 18 % |
| Tensile modulus | ISO527-2/1 | 1580 Mpa | |
| tensile strength | 屈服 | ASTMD638 | 37.9 Mpa |
| Tensile strain | 屈服 | ISO527-2 | 18 % |
| tensile strength | 断裂 | ASTMD638 | 35.2 Mpa |
| Flexural modulus | ISO178 | 1300 Mpa | |
| Wear factor - Washer | ASTMD3702Modified | 13.5 10^-10in^5-min/ft-lb-hr |
| physical property | Test Condition | Test Method | SABIC INNOVATIVE US/SP003 |
|---|---|---|---|
| Shrinkage rate | TD：24hr | ASTMD955 | 1.8to2.0 % |
| MD:24小时 | ISO294-4 | 1.0 % | |
| TD:24小时 | ISO294-4 | 1.9 % | |
| Water absorption rate | 24hr,50%RH | ASTMD570 | 0.20 % |
| Shrinkage rate | MD：24小时 | ASTMD955 | 0.90to1.1 % |
| Thermal performance | Test Condition | Test Method | SABIC INNOVATIVE US/SP003 |
|---|---|---|---|
| 1.8MPa,未退火,3.20mm | ASTMD648 | 146 °C | |
| Hot deformation temperature 4 | 0.45MPa,Unannealed,64.0mmSpan | ISO75-2/Bf | 134 °C |
| MD：-40到40°C | ISO11359-2 | 1.1E-04 cm/cm/°C | |
| TD：-40到40°C | ISO11359-2 | 1.1E-04 cm/cm/°C | |
| MD：-40到40°C | ASTME831 | 1.1E-04 cm/cm/°C | |
| 0.45MPa,未退火,3.20mm | ASTMD648 | 150 °C | |
| Hot deformation temperature 4 | 1.8MPa,未退火,64.0mm跨距 | ISO75-2/Af | 147 °C |
| TD：-40到40°C | ASTME831 | 1.1E-04 cm/cm/°C |