Technical Data Sheet
| physical property | Test Condition | Test Method | Test Result |
|---|
| Melt volume flow rate | | ISO 1133 | 25.0 cm³/10min |
| Shrinkage rate | | ISO 294-4 | 0.40to0.60 % |
| Shrinkage rate | | ISO 294-4 | 0.40to0.60 % |
| density | | ISO 1183 | 1.05 g/cm³ |
| hardness | Test Condition | Test Method | Test Result |
|---|
| ball-indentation hardness | | ISO 2039-1 | 105 MPa |
| flammability | Test Condition | Test Method | Test Result |
|---|
| burning rate | | ISO 3795 | 60 mm/min |
| UL flame retardant rating | | UL 94 | HB |
| Burning wire flammability index | | IEC 60695-2-12 | 700 °C |
| Mechanical properties | Test Condition | Test Method | Test Result |
|---|
| Tensile strain | | ISO 527-2/50 | 2.5 % |
| Tensile strain | | ISO 527-2/50 | >15 % |
| Flexural modulus | | ISO 178 | 2400 MPa |
| bending strength | | ISO 178 | 72.0 MPa |
| Tensile modulus | | ISO 527-2/1 | 2400 MPa |
| tensile strength | | ISO 527-2/50 | 47.0 MPa |
| Impact resistance | Test Condition | Test Method | Test Result |
|---|
| Charpy Notched Impact Strength | | ISO 179/1eA | 7.0 kJ/m² |
| Charpy Notched Impact Strength | | ISO 179/1eA | 17 kJ/m² |
| Impact strength of simply supported beam without notch | | ISO 179/1eU | 80 kJ/m² |
| Impact strength of simply supported beam without notch | | ISO 179/1eU | 90 kJ/m² |
| Impact strength of cantilever beam gap | | ISO 180/1A | 7.0 kJ/m² |
| Impact strength of cantilever beam gap | | ISO 180/1A | 17 kJ/m² |
| Electrical performance | Test Condition | Test Method | Test Result |
|---|
| relative permittivity | | IEC 60250 | 3.10 |
| relative permittivity | | IEC 60250 | 3.00 |
| Dissipation Factor | | IEC 60250 | 5E-03 |
| Dissipation Factor | | IEC 60250 | 8E-03 |
| Compared to the Leakage Tracking Index (CTI) | | IEC 60112 | PLC 0 |
| dielectric strength | | IEC 60243-1 | 33 kV/mm |
| Thermal performance | Test Condition | Test Method | Test Result |
|---|
| Heat distortion temperature | | ISO 75-2/B | 102 °C |
| Heat distortion temperature | | ISO 75-2/A | 98.0 °C |
| vicat | | ISO 306/B50 | 101 °C |
IMPORTANT NOTES: Plas.com collected the data in the data sheet from the material manufacturers. Plas.com makes the best effort to improve the accuracy of the data, but has no responsibility for the data. We strongly recommend verifying the validity of the data with the material manufacturers before making a final decision.
Compare