ABS ABS H605 ELIX Polymers, S. L.
--
--
--
--
--
--
--
--
--
--
--
--
--
--
--
--
--
--
Plastic Datasheets
Impact resistance | Test Condition | Test Method | ELIX Polymers, S. L./ABS H605 |
---|---|---|---|
Charpy Notched Impact Strength | 23°C | ISO 179/1eA | 17 kJ/m² |
-30°C | ISO 179/1eA | 7.0 kJ/m² | |
Impact strength of cantilever beam gap | -30°C | ISO 180/1A | 7.0 kJ/m² |
Impact strength of simply supported beam without notch | 23°C | ISO 179/1eU | 90 kJ/m² |
Impact strength of cantilever beam gap | 23°C | ISO 180/1A | 17 kJ/m² |
Impact strength of simply supported beam without notch | -30°C | ISO 179/1eU | 80 kJ/m² |
hardness | Test Condition | Test Method | ELIX Polymers, S. L./ABS H605 |
---|---|---|---|
ball-indentation hardness | ISO 2039-1 | 105 MPa |
Mechanical properties | Test Condition | Test Method | ELIX Polymers, S. L./ABS H605 |
---|---|---|---|
tensile strength | 屈服,23°C | ISO 527-2/50 | 47.0 MPa |
Flexural modulus | 23°C | ISO 178 | 2400 MPa |
Tensile strain | 屈服,23°C | ISO 527-2/50 | 2.5 % |
断裂,23°C | ISO 527-2/50 | >15 % | |
Tensile modulus | 23°C | ISO 527-2/1 | 2400 MPa |
bending strength | 23°C | ISO 178 | 72.0 MPa |
Electrical performance | Test Condition | Test Method | ELIX Polymers, S. L./ABS H605 |
---|---|---|---|
dielectric strength | 23°C,1.00mm | IEC 60243-1 | 33 kV/mm |
relative permittivity | 23°C,1MHz | IEC 60250 | 3.00 |
23°C,100Hz | IEC 60250 | 3.10 | |
Compared to the Leakage Tracking Index (CTI) | 解决方案A | IEC 60112 | PLC 0 |
Dissipation Factor | 23°C,100Hz | IEC 60250 | 5E-03 |
23°C,1MHz | IEC 60250 | 8E-03 |
flammability | Test Condition | Test Method | ELIX Polymers, S. L./ABS H605 |
---|---|---|---|
burning rate | 2.00mm | ISO 3795 | 60 mm/min |
Burning wire flammability index | 2.0mm | IEC 60695-2-12 | 700 °C |
UL flame retardant rating | 1.6mm | UL 94 | HB |
physical property | Test Condition | Test Method | ELIX Polymers, S. L./ABS H605 |
---|---|---|---|
Melt volume flow rate | 220°C/10.0kg | ISO 1133 | 25.0 cm³/10min |
Shrinkage rate | TD | ISO 294-4 | 0.40to0.60 % |
MD | ISO 294-4 | 0.40to0.60 % | |
density | ISO 1183 | 1.05 g/cm³ |
Thermal performance | Test Condition | Test Method | ELIX Polymers, S. L./ABS H605 |
---|---|---|---|
Heat distortion temperature | 1.8MPa,退火,HDT | ISO 75-2/A | 98.0 °C |
vicat | ISO 306/B50 | 101 °C | |
Heat distortion temperature | 0.45MPa,退火,HDT | ISO 75-2/B | 102 °C |