Technical Data Sheet
| physical property | Test Condition | Test Method | Test Result |
|---|
| density | | ISO 1183 | 1.36 g/cm³ |
| Shrinkage rate | | ISO 294-4 | 0.15to0.40 % |
| flammability | Test Condition | Test Method | Test Result |
|---|
| Limiting Oxygen Index | | ISO 4589-2 | 22 % |
| FMVSS flammability | | FMVSS302 | Passed |
| UL flame retardant rating | | UL 94 | HB |
| Mechanical properties | Test Condition | Test Method | Test Result |
|---|
| tensile strength | Yield | ISO 527-2 | 158 MPa |
| Tensile strain | Yield | ISO 527-2 | 3.0 % |
| Tensile strain | Break | ISO 527-2 | 3.0 % |
| Flexural modulus | | ISO 178 | 8100 MPa |
| bending strength | | ISO 178 | 225 MPa |
| Impact resistance | Test Condition | Test Method | Test Result |
|---|
| Impact strength of cantilever beam gap | | ISO 180/1A | 9.0 kJ/m² |
| Impact strength of cantilever beam gap | | ISO 180/1A | 11 kJ/m² |
| Electrical performance | Test Condition | Test Method | Test Result |
|---|
| Volume resistivity | | ISO 1325 | 1E+15 ohms·cm |
| dielectric strength | | ASTM D149 | 11 kV/mm |
| Compared to the Leakage Tracking Index (CTI) | | 内部方法 | PLC 0 |
| Thermal performance | Test Condition | Test Method | Test Result |
|---|
| Heat distortion temperature | | ISO 75-2/A | 200 °C |
| melting temperature | | ASTM D789 | 220 °C |
| Linear coefficient of thermal expansion | | ASTM D696 | 5.3E-05 cm/cm/°C |
IMPORTANT NOTES: Plas.com collected the data in the data sheet from the material manufacturers. Plas.com makes the best effort to improve the accuracy of the data, but has no responsibility for the data. We strongly recommend verifying the validity of the data with the material manufacturers before making a final decision.