PA6 230 GH Chem Polymer Company
--
--
--
--
--
--
--
--
--
--
--
--
--
--
--
--
--
--
Plastic Datasheets
| Impact resistance | Test Condition | Test Method | Chem Polymer Company/230 GH |
|---|---|---|---|
| Impact strength of cantilever beam gap | 23°C | ISO 180/1A | 11 kJ/m² |
| -40°C | ISO 180/1A | 9.0 kJ/m² |
| Mechanical properties | Test Condition | Test Method | Chem Polymer Company/230 GH |
|---|---|---|---|
| Tensile strain | 断裂 | ISO 527-2 | 3.0 % |
| 屈服 | ISO 527-2 | 3.0 % | |
| tensile strength | 屈服 | ISO 527-2 | 158 MPa |
| Flexural modulus | ISO 178 | 8100 MPa | |
| bending strength | ISO 178 | 225 MPa |
| Electrical performance | Test Condition | Test Method | Chem Polymer Company/230 GH |
|---|---|---|---|
| dielectric strength | 3.00mm | ASTM D149 | 11 kV/mm |
| Compared to the Leakage Tracking Index (CTI) | 内部方法 | PLC 0 | |
| Volume resistivity | ISO 1325 | 1E+15 ohms·cm |
| flammability | Test Condition | Test Method | Chem Polymer Company/230 GH |
|---|---|---|---|
| FMVSS flammability | FMVSS302 | Passed | |
| Limiting Oxygen Index | ISO 4589-2 | 22 % | |
| UL flame retardant rating | 0.8mm | UL 94 | HB |
| physical property | Test Condition | Test Method | Chem Polymer Company/230 GH |
|---|---|---|---|
| Shrinkage rate | ISO 294-4 | 0.15to0.40 % | |
| density | ISO 1183 | 1.36 g/cm³ |
| Thermal performance | Test Condition | Test Method | Chem Polymer Company/230 GH |
|---|---|---|---|
| melting temperature | ASTM D789 | 220 °C | |
| Heat distortion temperature | 1.8MPa,未退火，HDT | ISO 75-2/A | 200 °C |
| Linear coefficient of thermal expansion | MD | ASTM D696 | 5.3E-05 cm/cm/°C |