PP N-Z30S

Properties:
It has medium to high flow performance
high monofilament strength
good flowability
good processability
stable product cross-sectional shape
recommended processing conditions
and is used for BCF process. The recommended spinning temperature is 230-290 ℃
the recommended side blowing temperature is 15 ℃
the wind speed is 1-1
2m
min
and it is best to control the side blowing humidity between 50-70%. It is recommended to use high-speed spinning
low draft process
and water bath stretching (125-135 ℃) for cigarette tow process For non-woven fabric forming process
recommended plasticizing temperature is 250-290 ℃
Usages:
This product is a fiber grade homopolymer polypropylene resin suitable for high-speed spinning
artificial fibers
BCF expanded yarn
and CF spinning. It is mainly used for various types of packaging ropes
belts
luggage belts
car safety belts
mattress edging
cigarette tow
etc
Compare

Technical Data Sheet

Basic performance	Test Condition	Test Method	Test Result
melt mass-flow rate			优等｜25.0±3.0 g/10min
	melt mass-flow rate			一等｜25.0±3.0 g/10min
	melt mass-flow rate	melt mass-flow rate			合格｜25.0±5.0 g/10min

Mechanical properties	Test Condition	Test Method	Test Result
Izod notched impact strength			优等｜≥28 J/m
	Izod notched impact strength			一等｜≥19 J/m
	Izod notched impact strength	Izod notched impact strength			合格｜≥9 J/m
tensile yield strength			优等｜≥32 MPa
	tensile yield strength			一等｜≥30 MPa
	tensile yield strength	tensile yield strength			合格｜≥30 MPa

Other performance	Test Condition	Test Method	Test Result
Powder ash content			一等｜≤0.02 %
Powder ash content	Powder ash content			合格｜≤0.02 %
cleanliness			一等｜≤10 个/kg
cleanliness	cleanliness			合格｜≤20 个/kg
isotactic index			优等｜≥96 %
	isotactic index			一等｜≥96 %
	isotactic index	isotactic index			合格｜≥96 %
Powder ash content			优等｜≤0.02 %
cleanliness			优等｜≤5 个/kg

IMPORTANT NOTES: Plas.com collected the data in the data sheet from the material manufacturers. Plas.com makes the best effort to improve the accuracy of the data, but has no responsibility for the data. We strongly recommend verifying the validity of the data with the material manufacturers before making a final decision.