Technical Data Sheet
| physical property | Test Condition | Test Method | Test Result |
|---|
| density | | ASTM D1505 | 1.19 g/cm³ |
| Water absorption rate | | ASTM D570 | 0.50 % |
| optical performance | Test Condition | Test Method | Test Result |
|---|
| Transmittance | | ASTM D1003 | 92.0 % |
| Haze ratio | | ASTM D1003 | 1.0 % |
| UV Transmittance | | | 89 % |
| gloss | | ASTM D2457 | 161 |
| refractive index | | ASTM D542 | 1.545 |
| Supplementary Information | Test Condition | Test Method | Test Result |
|---|
| SurfaceEnergy-Polar | | ASTM D5946 | 45 dyne/cm |
| Mechanical properties | Test Condition | Test Method | Test Result |
|---|
| Abrasion | | ASTM D1044 | 23%Haze |
| Impact resistance | Test Condition | Test Method | Test Result |
|---|
| Dart impact | | ASTM D3763 | 4.60 J |
| film | Test Condition | Test Method | Test Result |
|---|
| elongation | | ASTM D882 | 180 % |
| Tensile strain | | ASTM D882 | 200 % |
| Dart impact | | ASTM D1709A | 910 g |
| Dart impact | | ASTM D1709A | 870 g |
| Dart impact | | ASTM D1709A | 880 g |
| Elmendorf tear strength | | ASTM D1922 | 520 g |
| Elmendorf tear strength | | ASTM D1922 | 580 g |
| Tear resistance of pants | | ISO 6383-1 | 11.0 N/mm |
| Tear resistance of pants | | ISO 6383-1 | 11.0 N/mm |
| OTr | | ASTM D3985 | 32 cm³·mm/m²/atm/24hr |
| Water Vapor Transmission Rate | | ASTMF1249 | 4.0 g/m²/24hr |
| Water Vapor Transmission Rate | | ASTMF1249 | 11 g/m²/24hr |
| Carbon dioxide transmittance | | ASTM D1434 | 150 cm³·mm/m²/atm/24hr |
| PPTTearResistance | | ASTM D2582 | 42 N |
| film thickness | | ASTM D374 | 250 µm |
| Tensile modulus | | ASTM D882 | 1460 MPa |
| Tensile modulus | | ASTM D882 | 1380 MPa |
| tensile strength | | ASTM D882 | 41.0 MPa |
| tensile strength | | ASTM D882 | 40.0 MPa |
| tensile strength | | ASTM D882 | 59.0 MPa |
| tensile strength | | ASTM D882 | 52.0 MPa |
| Tensile strain | | ASTM D882 | 7.0 % |
| Tensile strain | | ASTM D882 | 7.0 % |
| PPTTearResistance | | ASTM D2582 | 56 N |
| tear strength | | ASTM D1938 | 410 gf |
| tear strength | | ASTM D1938 | 310 gf |
| Thermal performance | Test Condition | Test Method | Test Result |
|---|
| specific heat | | DSC | 2250 J/kg/°C |
| specific heat | | DSC | 2400 J/kg/°C |
| specific heat | | DSC | 2570 J/kg/°C |
| brittle temperature | | ASTM D746 | <-60.0 °C |
| Glass Transition Temperature | | DSC | 110 °C |
| Linear coefficient of thermal expansion | | ASTM D696 | 8.8E-05 cm/cm/°C |
| specific heat | | DSC | 1710 J/kg/°C |
| specific heat | | DSC | 1890 J/kg/°C |
IMPORTANT NOTES: Plas.com collected the data in the data sheet from the material manufacturers. Plas.com makes the best effort to improve the accuracy of the data, but has no responsibility for the data. We strongly recommend verifying the validity of the data with the material manufacturers before making a final decision.