Copolyester Tritan™ MP100 Eastman Chemical Company
--
--
--
--
--
--
--
--
--
--
--
--
--
--
--
--
--
--
Plastic Datasheets
Impact resistance | Test Condition | Test Method | Eastman Chemical Company/Tritan™ MP100 |
---|---|---|---|
Dart impact | 23°C,TotalEnergy | ASTM D3763 | 4.60 J |
Supplementary Information | Test Condition | Test Method | Eastman Chemical Company/Tritan™ MP100 |
---|---|---|---|
SurfaceEnergy-Polar | 23°C | ASTM D5946 | 45 dyne/cm |
film | Test Condition | Test Method | Eastman Chemical Company/Tritan™ MP100 |
---|---|---|---|
Dart impact | -30°C,250µm | ASTM D1709A | 910 g |
-18°C,250µm | ASTM D1709A | 870 g | |
tensile strength | Break,250µm | ASTM D882 | 52.0 MPa |
Water Vapor Transmission Rate | 23°C,100%RH,250µm | ASTMF1249 | 4.0 g/m²/24hr |
film thickness | ASTM D374 | 250 µm | |
Tensile modulus | 250µm,TD | ASTM D882 | 1380 MPa |
tensile strength | Yield,250µm | ASTM D882 | 40.0 MPa |
elongation | 断裂,250µm | ASTM D882 | 180 % |
Carbon dioxide transmittance | 23°C,250.0µm | ASTM D1434 | 150 cm³·mm/m²/atm/24hr |
PPTTearResistance | MD:23°C,250.0µm | ASTM D2582 | 42 N |
Tensile strain | Yield,250µm | ASTM D882 | 7.0 % |
tensile strength | 屈服,250µm | ASTM D882 | 41.0 MPa |
tear strength | MD,SplitTearMethod:23°C,250.0µm | ASTM D1938 | 410 gf |
TD,SplitTearMethod:23°C,250.0µm | ASTM D1938 | 310 gf | |
Tensile modulus | 250µm,MD | ASTM D882 | 1460 MPa |
Water Vapor Transmission Rate | 38°C,100%RH,250µm | ASTMF1249 | 11 g/m²/24hr |
OTr | 23°C,250µm,50%RH | ASTM D3985 | 32 cm³·mm/m²/atm/24hr |
Dart impact | 23°C,250µm | ASTM D1709A | 880 g |
Tensile strain | Break,250µm | ASTM D882 | 200 % |
Elmendorf tear strength | 250µm,MD | ASTM D1922 | 520 g |
PPTTearResistance | TD:23°C,250.0µm | ASTM D2582 | 56 N |
Tensile strain | Yield,250µm,MD | ASTM D882 | 7.0 % |
Elmendorf tear strength | 250µm,TD | ASTM D1922 | 580 g |
Tear resistance of pants | MD:250µm | ISO 6383-1 | 11.0 N/mm |
TD:250µm | ISO 6383-1 | 11.0 N/mm |
Mechanical properties | Test Condition | Test Method | Eastman Chemical Company/Tritan™ MP100 |
---|---|---|---|
Abrasion | 23°C | ASTM D1044 | 23%Haze |
optical performance | Test Condition | Test Method | Eastman Chemical Company/Tritan™ MP100 |
---|---|---|---|
UV Transmittance | 89 % | ||
Transmittance | Total,250µm | ASTM D1003 | 92.0 % |
refractive index | ASTM D542 | 1.545 | |
gloss | 60°,250µm | ASTM D2457 | 161 |
Haze ratio | 250µm | ASTM D1003 | 1.0 % |
physical property | Test Condition | Test Method | Eastman Chemical Company/Tritan™ MP100 |
---|---|---|---|
density | ASTM D1505 | 1.19 g/cm³ | |
Water absorption rate | 23°C,24hr | ASTM D570 | 0.50 % |
Thermal performance | Test Condition | Test Method | Eastman Chemical Company/Tritan™ MP100 |
---|---|---|---|
specific heat | 60°C | DSC | 1710 J/kg/°C |
Glass Transition Temperature | DSC | 110 °C | |
specific heat | 150°C | DSC | 2250 J/kg/°C |
200°C | DSC | 2400 J/kg/°C | |
100°C | DSC | 1890 J/kg/°C | |
brittle temperature | ASTM D746 | <-60.0 °C | |
specific heat | 250°C | DSC | 2570 J/kg/°C |
Linear coefficient of thermal expansion | MD:23°C | ASTM D696 | 8.8E-05 cm/cm/°C |