Technical Data Sheet
| thermal performance | Test Condition | Test Method | Test Result |
|---|
| Heat Deflection Temperature | 1.8MPa,未退火 | ISO 75-2/A | 250 °C |
| melting temperature | | ISO 11357-3 | 285 °C |
| Linear coefficient of thermal expansion | MD | ISO 11359-2 | 4.8E-05 cm/cm/°C |
| Linear coefficient of thermal expansion | TD | ISO 11359-2 | 9E-05 cm/cm/°C |
| flammability | Test Condition | Test Method | Test Result |
|---|
| UL flame retardant rating | 1.5mm | UL 94 | HB |
| Physical properties | Test Condition | Test Method | Test Result |
|---|
| density | | ISO 1183 | 1.44 g/cm³ |
| shrinkage rate | TD | ISO 294-4 | 0.80 % |
| shrinkage rate | MD | ISO 294-4 | 0.30 % |
| water absorption rate | 饱和,23°C | ISO 62 | 1.4 % |
| water absorption rate | 平衡,23°C,50%RH | ISO 62 | 0.15 % |
| Electrical performance | Test Condition | Test Method | Test Result |
|---|
| dielectric strength | | IEC 60243-1 | 35 kV/mm |
| mechanical properties | Test Condition | Test Method | Test Result |
|---|
| tensile modulus | | ISO 527-2/1A/1 | 8400 MPa |
| bending strength | 23°C | ISO 178 | 180 MPa |
| tensile strength | Break | ISO 527-2/1A/5 | 110 MPa |
| Tensile strain | Break | ISO 527-2/1A/5 | 2.8 % |
| flexural modulus | 23°C | ISO 178 | 7600 MPa |
| impact performance | Test Condition | Test Method | Test Result |
|---|
| Charpy Notched Impact Strength | 23°C | ISO 179/1eA | 10 kJ/m² |
| Impact strength of cantilever beam gap | 23°C | ISO 180/1A | 10 kJ/m² |
IMPORTANT NOTES: Plas.com collected the data in the data sheet from the material manufacturers. Plas.com makes the best effort to improve the accuracy of the data, but has no responsibility for the data. We strongly recommend verifying the validity of the data with the material manufacturers before making a final decision.