PCT Thermx® CGT33 CELANESE USA
--
--
--
--
--
--
--
--
--
--
--
--
--
--
--
--
--
--
Plastic Datasheets
Impact resistance | Test Condition | Test Method | CELANESE USA/Thermx® CGT33 |
---|---|---|---|
Charpy Notched Impact Strength | 23°C | ISO 179/1eA | 10 kJ/m² |
Impact strength of cantilever beam gap | 23°C | ISO 180/1A | 10 kJ/m² |
Mechanical properties | Test Condition | Test Method | CELANESE USA/Thermx® CGT33 |
---|---|---|---|
Flexural modulus | 23°C | ISO 178 | 7600 MPa |
Tensile modulus | ISO 527-2/1A/1 | 8400 MPa | |
tensile strength | 断裂 | ISO 527-2/1A/5 | 110 MPa |
Tensile strain | 断裂 | ISO 527-2/1A/5 | 2.8 % |
bending strength | 23°C | ISO 178 | 180 MPa |
Electrical performance | Test Condition | Test Method | CELANESE USA/Thermx® CGT33 |
---|---|---|---|
dielectric strength | IEC 60243-1 | 35 kV/mm |
flammability | Test Condition | Test Method | CELANESE USA/Thermx® CGT33 |
---|---|---|---|
UL flame retardant rating | 1.5mm | UL 94 | HB |
physical property | Test Condition | Test Method | CELANESE USA/Thermx® CGT33 |
---|---|---|---|
Shrinkage rate | TD | ISO 294-4 | 0.80 % |
MD | ISO 294-4 | 0.30 % | |
Water absorption rate | 平衡,23°C,50%RH | ISO 62 | 0.15 % |
饱和,23°C | ISO 62 | 1.4 % | |
density | ISO 1183 | 1.44 g/cm³ |
Thermal performance | Test Condition | Test Method | CELANESE USA/Thermx® CGT33 |
---|---|---|---|
melting temperature | ISO 11357-3 | 285 °C | |
Heat distortion temperature | 1.8MPa,未退火,HDT | ISO 75-2/A | 250 °C |
Linear coefficient of thermal expansion | MD | ISO 11359-2 | 4.8E-05 cm/cm/°C |
TD | ISO 11359-2 | 9E-05 cm/cm/°C |