HDPE HD12BK
0
- Properties:Good resistance to environmental stress cracking and wear resistance
- Usages:Used for manufacturing pressure pipes and fittingsfor drinking waterdrainagesewage treatmentand slurry pipelines
CompareTechnical Data Sheet
| Basic performance | Test Condition | Test Method | Test Result |
|---|---|---|---|
| density | ISO 1183 | 951 kg/m | |
| Carbon black content | ISO 6964 | 2.25 % | |
| density | ISO 1872/1 | 953 kg/m | |
| melt mass-flow rate | ISO 1133: Condition 18 | 0.58 g/10min |
| Mechanical properties | Test Condition | Test Method | Test Result |
|---|---|---|---|
| ISO TR9080(97.5% LCL) | 8.0 MPa | ||
| tensile yield stress | ISO/R527:Type 2,Speed D | 23 MPa | |
| elongation | Break | ISO/R527:Type 2,Speed D | ＞600 % |
| Flexural modulus | ISO 178 | 850 MPa | |
| Environmental stress cracking resistance | ASTM D-1693B | ＞1000 Hours |
| Other performance | Test Condition | Test Method | Test Result |
|---|---|---|---|
| oxidation induction time | ISO TR10837 | ＞20 min | |
| ISO TR10837 | ＞40 min |
| Electrical performance | Test Condition | Test Method | Test Result |
|---|---|---|---|
| Volume resistivity | Ω.cm | BS 2782:230 A ＞10 |
| Thermal performance | Test Condition | Test Method | Test Result |
|---|---|---|---|
| vicat | ISO 306 A | 120 ℃ | |
| thermal conductivity | W/m℃ | BS 874(at 23℃) 0.4 | |
| Linear thermal expansion | ASTM D-696(20-60℃) | 1.5×10 ℃ | |
| brittle temperature | ASTM D-746 | ＜-70 ℃ |
IMPORTANT NOTES: Plas.com collected the data in the data sheet from the material manufacturers. Plas.com makes the best effort to improve the accuracy of the data, but has no responsibility for the data. We strongly recommend verifying the validity of the data with the material manufacturers before making a final decision.