PA610 LNP™ LUBRICOMP™ QFL-4036
144
- Properties:Thermal stabilityConductiveGlass fiber reinforced
- Usages:Electronic and Electrical ApplicationsFitness equipment
Compare
View PricesTechnical Data Sheet
| physical property | Test Condition | Test Method | Test Result |
|---|---|---|---|
| Shrinkage rate | ASTM D955 | 0.70 % | |
| ISO 294-4 | 0.70 % | ||
| ISO 294-4 | 0.17 % | ||
| Water absorption rate | ASTM D570 | 0.14 % | |
| ISO 62 | 0.22 % | ||
| Shrinkage rate | ASTM D955 | 0.20 % |
| Mechanical properties | Test Condition | Test Method | Test Result |
|---|---|---|---|
| Flexural modulus | ASTM D790 | 8480 Mpa | |
| ISO 178 | 9700 Mpa | ||
| bending strength | ASTM D790 | 221 Mpa | |
| ISO 178 | 228 Mpa | ||
| coefficient of friction | ASTM D3702Modified | 0.71 | |
| ASTM D3702Modified | 0.52 | ||
| Wear factor | ASTM D3702Modified | 15.0 10^-10in^5-min/ft-lb-hr | |
| Tensile modulus | ASTM D638 | 11000 Mpa | |
| ISO 527-2/1 | 9800 Mpa | ||
| tensile strength | ASTM D638 | 149 Mpa | |
| ISO 527-2 | 150 Mpa | ||
| elongation | ASTMD638 | 2.6 % |
| Impact resistance | Test Condition | Test Method | Test Result |
|---|---|---|---|
| Suspended wall beam without notch impact strength | ASTM D4812 | 940 J/m | |
| ISO 180/1U | 65 kJ/m² | ||
| Dart impact | ASTM D3763 | 8.50 J | |
| ISO 6603-2 | 3.19 J |
| Thermal performance | Test Condition | Test Method | Test Result |
|---|---|---|---|
| Heat distortion temperature | ASTM D648 | 224 °C | |
| ASTM D648 | 216 °C | ||
| ISO 75-2/Af | 211 °C | ||
| Linear coefficient of thermal expansion | ASTME831 | 2.9E-05 cm/cm/°C | |
| ASTME831 | 7.4E-05 cm/cm/°C | ||
| ISO 11359-2 | 7.5E-05 cm/cm/°C |
IMPORTANT NOTES: Plas.com collected the data in the data sheet from the material manufacturers. Plas.com makes the best effort to improve the accuracy of the data, but has no responsibility for the data. We strongly recommend verifying the validity of the data with the material manufacturers before making a final decision.