Material Comparison
Product Info
Product Name
Brand Name
Usages
Properties
Certificates
PA610 QFL-4036 SABIC INNOVATIVE US
LNP™ LUBRICOMP™
Electronic and Electrical、Fitness equipment
Thermal stability、Conductive、Glass fiber reinforced
--
--
--
--
--
--
--
--
--
--
--
--
--
--
--
Plastic Datasheets
| Thermal Properties | Test Condition | Test Method | SABIC INNOVATIVE US/QFL-4036 |
|---|---|---|---|
| Linear thermal expansion coefficient | MD:-40到40°C | ASTME831,ISO11359-2 | 2.9E-05 cm/cm/°C |
| Heat Deflection Temperature | 1.8MPa,未退火,64.0mm跨距5 | ISO75-2/Af | 211 °C |
| 0.45MPa,未退火,3.20mm | ASTMD648 | 224 °C | |
| 1.8MPa,未退火,3.20mm | ASTMD648 | 216 °C | |
| Linear thermal expansion coefficient | TD:-40到40°C | ASTME831 | 7.4E-05 cm/cm/°C |
| TD:-40到40°C | ISO11359-2 | 7.5E-05 cm/cm/°C |
| Mechanical Properties | Test Condition | Test Method | SABIC INNOVATIVE US/QFL-4036 |
|---|---|---|---|
| Flexural Strength | -- | ASTMD790 | 221 Mpa |
| Flexural Modulus | -- | ISO178 | 9700 Mpa |
| Tensile Modulus | --3 | ASTMD638 | 11000 Mpa |
| Flexural Strength | -- | ISO178 | 228 Mpa |
| Coefficient of Friction | Static | ASTMD3702Modified | 0.52 |
| Tensile Strength | 断裂 | ISO527-2 | 150 Mpa |
| Specific Wear Rate | ASTMD3702Modified | 15.0 10^-10in^5-min/ft-lb-hr | |
| Tensile Modulus | -- | ISO527-2/1 | 9800 Mpa |
| Coefficient of Friction | Dynamic | ASTMD3702Modified | 0.71 |
| Flexural Modulus | -- | ASTMD790 | 8480 Mpa |
| Tensile Strength | 断裂 | ASTMD638 | 149 Mpa |
| Tensile Elongation | 断裂 | ASTMD638,ISO527-2 | 2.6 % |
| Physical | Test Condition | Test Method | SABIC INNOVATIVE US/QFL-4036 |
|---|---|---|---|
| Moisture Absorption | 平衡,23°C,50%RH | ISO62 | 0.22 % |
| 24hr,50%RH | ASTMD570 | 0.14 % | |
| Modeling Shrinkage | TD:24小时 | ASTMD955 | 0.70 % |
| TD:24小时 | ISO294-4 | 0.70 % | |
| MD:24小时 | ISO294-4 | 0.17 % | |
| MD:24小时 | ASTMD955 | 0.20 % |
| Impact Properties | Test Condition | Test Method | SABIC INNOVATIVE US/QFL-4036 |
|---|---|---|---|
| Unnotched Izod Impact Strength | 23°C | ASTMD4812 | 940 J/m |
| Instrumented Dart Impact | -- | ISO6603-2 | 3.19 J |
| Unnotched Izod Impact Strength | 23°C4 | ISO180/1U | 65 kJ/m² |
| Instrumented Dart Impact | 23°C,EnergyatPeakLoad | ASTMD3763 | 8.50 J |