ABS 3000D TAIDA TAIWAN

Form：Granules | Grade：Withdrawal level

Properties:

Chemical resistanceHigh impact resistanceUltra high impact resistaWidely used for extrusionUltra high impact strengtGood processabilityExcellent hot forming

Typical Applications:

ToolboxPlastic boxUsed for luggageLocomotive partsLow temperature productsHelmetBus boxheelControlled pipe fittings etcTool/parts boxLeather suitcase

Supplier(0)

Product Description

Certificates(4)

Datasheet

Product Description

Typical Applications:	Toolbox \| Plastic box \| Used for luggage \| Locomotive parts \| Low temperature products \| Helmet \| Bus box \| heel \| Controlled pipe fittings \| etc \| Tool/parts box \| Leather suitcase
Properties:	Chemical resistance \| High impact resistance \| Ultra high impact resista \| Widely used for extrusion \| Ultra high impact strengt \| Good processability \| Excellent hot forming

Certificates

TDS

TDS_ISO

Technical Data Sheet

impact performance	Test Condition	Test Method	Test Result	Test Unit
Impact strength of cantilever beam gap	23°C,3.18mm	ASTM D256	440	J/m
Impact strength of cantilever beam gap	Impact strength of cantilever beam gap	23°C,6.35mm	ASTM D256	390	J/m
flammability	Test Condition	Test Method	Test Result	Test Unit
UL flame retardant rating	1.6mm	UL 94	HB
Basic Performance	Test Condition	Test Method	Test Result	Test Unit
melt mass-flow rate	200℃/5kg	ASTM D-1238	1.0	g/10min
melt mass-flow rate	melt mass-flow rate	200℃/5kg	ASTM D-1238	10	g/10min
density		ASTM D-792	1.03
Water absorption rate		ASTM D-570	0.3	wt%
mechanical properties	Test Condition	Test Method	Test Result	Test Unit
tensile strength	1/8"，Break	ASTM D-638	5100	psi
Elongation at Break	1/8"	ASTM D-638	40	%
bending strength	23℃ 2.8mm/min	ASTM D-790	600	kg/cm2
bending strength	bending strength	23℃ 2.8mm/min	ASTM D-790	8500	psi
flexural coefficient	23℃ 2.8mm/min	ASTM D-790	21000	kg/cm2
flexural coefficient	flexural coefficient	23℃ 2.8mm/min	ASTM D-790	300000	psi
Rockwell hardness			102
Impact strength of cantilever beam gap	23℃1/2"	ASTM D-256	31 (5.5)	kg.cm/cm(ft.1b/in)
Impact strength of cantilever beam gap	Impact strength of cantilever beam gap	1/8" 23℃	ASTM D-256	45 (7.0)	kg.cm/cm(ft.1b/in)
tensile strength	23℃，Yield	ASTM D-638	410	kg/cm2
	tensile strength	23℃，Yield	ASTM D-256	5800	psi
		tensile strength	1/8"，Break	ASTM D-638	360	kg/cm2
			tensile strength	Yield,23°C,3.18mm	ASTM D638	38.6	Mpa
			tensile strength	tensile strength	Break,23°C,3.18mm	ASTM D638	35.2	Mpa
elongation	Break,23°C,3.18mm	ASTM D638	40	%
Bending modulus	23°C	ASTM D790	2070	Mpa
bending strength	Yield,23°C	ASTM D790	58.6	Mpa
thermal performance	Test Condition	Test Method	Test Result	Test Unit
Hot deformation temperature	Unannealed	ASTM D-648	86 (187)	℃(F)
Vicat softening temperature		ASTM D-1525	101	°C
UL flame retardant rating		UL 94	HB
Hot deformation temperature	1.8MPa,Unannealed,12.7mm	ASTM D648	86.0	°C
Vicat softening temperature		ASTM D15254	101	°C
Physical properties	Test Condition	Test Method	Test Result	Test Unit
Shrinkage rate		ASTM D-955	0.4	%
Water absorption rate	24hr	ASTM D570	<0.30	%
density		ASTM D792	1.03	g/cm³
melt mass-flow rate	200°C/5.0kg	ASTM D1238	1.0	g/10min
melt mass-flow rate	melt mass-flow rate	220°C/10.0kg	ASTM D1238	10	g/10min
Shrinkage rate	MD	ASTM D955	<0.40	%
hardness	Test Condition	Test Method	Test Result	Test Unit
Rockwell hardness	R-Sale,23°C	ASTM D785	102

IMPORTANT NOTES: Plas.com collected the data in the data sheet from the material manufacturers. Plas.com makes the best effort to improve the accuracy of the data, but has no responsibility for the data. We strongly recommend verifying the validity of the data with the material manufacturers before making a final decision.