ABS 3000D TAIDA TAIWAN
TAITALAC®
Toolbox、Plastic box、Used for luggage、Locomotive parts、Low temperature products、Helmet、Bus box、heel、Controlled pipe fittings,、Tool/parts box、Leather suitcase
Chemical resistance、High impact resistance、Ultra high impact resista、Widely used for extrusion、Ultra high impact strengt、Good processability、Excellent hot forming
UL
TDS
TDS_ISO
UL
--
--
--
--
--
--
--
--
--
--
--
--
--
--
--
Plastic Datasheets
| Impact resistance | Test Condition | Test Method | TAIDA TAIWAN/3000D |
|---|---|---|---|
| Impact strength of cantilever beam gap | 23°C,6.35mm | ASTMD256 | 390 J/m |
| 23°C,3.18mm | ASTMD256 | 440 J/m |
| hardness | Test Condition | Test Method | TAIDA TAIWAN/3000D |
|---|---|---|---|
| Rockwell hardness | R计秤,23°C | ASTMD785 | 102 |
| Basic performance | Test Condition | Test Method | TAIDA TAIWAN/3000D |
|---|---|---|---|
| Water absorption rate | ASTM D-570 | 0.3 wt% | |
| density | ASTM D-792 | 1.03 | |
| melt mass-flow rate | 200℃/5kg | ASTM D-1238 | 10 g/10min |
| Mechanical properties | Test Condition | Test Method | TAIDA TAIWAN/3000D |
|---|---|---|---|
| IZOD notch impact strength | 23℃1/2" | ASTM D-256 | 31 (5.5) kg.cm/cm(ft.1b/in) |
| tensile strength | 屈服,23°C,3.18mm | ASTMD638 | 38.6 Mpa |
| Flexural Strength | 23℃ 2.8mm/min | ASTM D-790 | 600 kg/cm2 |
| IZOD notch impact strength | 1/8" 23℃ | ASTM D-256 | 45 (7.0) kg.cm/cm(ft.1b/in) |
| Tensile strength at the point of surrender | 23℃ | ASTM D-638 | 410 kg/cm2 |
| Tensile strength at fracture point | 1/8" | ASTM D-638 | 360 kg/cm2 |
| Tensile strength at the point of surrender | 23℃ | ASTM D-256 | 5800 psi |
| Tensile strength 2 | Break,23°C,3.18mm | ASTMD638 | 35.2 Mpa |
| elongation | 断裂,23°C,3.18mm | ASTMD638 | 40 % |
| Flexural coefficient | 23℃ 2.8mm/min | ASTM D-790 | 300000 psi |
| Flexural modulus | 23°C | ASTMD790 | 2070 Mpa |
| bending strength | 屈服,23°C | ASTMD790 | 58.6 Mpa |
| Flexural coefficient | 23℃ 2.8mm/min | ASTM D-790 | 21000 kg/cm2 |
| Flexural Strength | 23℃ 2.8mm/min | ASTM D-790 | 8500 psi |
| Rockwell hardness | 102 | ||
| elongation at break | 1/8" | ASTM D-638 | 40 % |
| Tensile strength at fracture point | 1/8" | ASTM D-638 | 5100 psi |
| flammability | Test Condition | Test Method | TAIDA TAIWAN/3000D |
|---|---|---|---|
| FlameRating | 1.6mm | UL94 | HB |
| physical property | Test Condition | Test Method | TAIDA TAIWAN/3000D |
|---|---|---|---|
| melt mass-flow rate | 200°C/5.0kg | ASTMD1238 | 1.0 g/10min |
| density | ASTMD792 | 1.03 g/cm³ | |
| Shrinkage rate | ASTM D-955 | 0.4 % | |
| Water absorption rate | 24hr | ASTMD570 | <0.30 % |
| Shrinkage rate | MD | ASTMD955 | <0.40 % |
| melt mass-flow rate | 220°C/10.0kg | ASTMD1238 | 10 g/10min |
| Thermal performance | Test Condition | Test Method | TAIDA TAIWAN/3000D |
|---|---|---|---|
| 未退火 | ASTM D-648 | 86 (187) ℃(F) | |
| 1.8MPa,未退火,12.7mm | ASTMD648 | 86.0 °C | |
| vicat | ASTM D-1525 | 101 °C | |
| ASTMD15254 | 101 °C | ||
| UL flame retardant rating | UL94 | HB |