ABS Romiloy® 1035 F ROMIRA GERMANY
0
CompareTechnical Data Sheet
| physical property | Test Condition | Test Method | Test Result |
|---|---|---|---|
| melt mass-flow rate | ISO 1133 | 25 g/10min | |
| Shrinkage rate | ISO 294-4 | 0.40to0.70 % | |
| Water absorption rate | ISO 62 | 0.20 % | |
| density | ISO 1183 | 1.13 g/cm³ |
| flammability | Test Condition | Test Method | Test Result |
|---|---|---|---|
| UL flame retardant rating | UL 94 | HB |
| Mechanical properties | Test Condition | Test Method | Test Result |
|---|---|---|---|
| tensile strength | ISO 527-2/50 | 55.0 MPa | |
| Tensile strain | ISO 527-2/50 | 85 % | |
| Tensile modulus | ISO 527-2/1 | 2150 MPa | |
| bending strength | ISO 178 | 83.0 MPa | |
| Flexural modulus | ISO 178 | 2200 MPa |
| Impact resistance | Test Condition | Test Method | Test Result |
|---|---|---|---|
| Impact strength of simply supported beam without notch | ISO 179/1eU | 无断裂 | |
| Charpy Notched Impact Strength | ISO 179/1eA | 38 kJ/m² |
| Thermal performance | Test Condition | Test Method | Test Result |
|---|---|---|---|
| Heat distortion temperature | ISO 75-2/A | 100 °C | |
| vicat | ISO 306/B50 | 121 °C | |
| Linear coefficient of thermal expansion | ISO 11359-2 | 8.5E-05 cm/cm/°C |
IMPORTANT NOTES: Plas.com collected the data in the data sheet from the material manufacturers. Plas.com makes the best effort to improve the accuracy of the data, but has no responsibility for the data. We strongly recommend verifying the validity of the data with the material manufacturers before making a final decision.