ABS Romiloy® 1035 F ROMIRA GERMANY
--
--
--
--
--
--
--
--
--
--
--
--
--
--
--
--
--
--
Plastic Datasheets
| Impact resistance | Test Condition | Test Method | ROMIRA GERMANY/Romiloy® 1035 F |
|---|---|---|---|
| Charpy Notched Impact Strength | 23°C | ISO 179/1eA | 38 kJ/m² |
| Impact strength of simply supported beam without notch | 23°C | ISO 179/1eU | 无断裂 |
| Mechanical properties | Test Condition | Test Method | ROMIRA GERMANY/Romiloy® 1035 F |
|---|---|---|---|
| tensile strength | 屈服,23°C | ISO 527-2/50 | 55.0 MPa |
| Flexural modulus | 23°C | ISO 178 | 2200 MPa |
| Tensile strain | 断裂,23°C | ISO 527-2/50 | 85 % |
| Tensile modulus | 23°C | ISO 527-2/1 | 2150 MPa |
| bending strength | 23°C | ISO 178 | 83.0 MPa |
| flammability | Test Condition | Test Method | ROMIRA GERMANY/Romiloy® 1035 F |
|---|---|---|---|
| UL flame retardant rating | 1.6mm | UL 94 | HB |
| physical property | Test Condition | Test Method | ROMIRA GERMANY/Romiloy® 1035 F |
|---|---|---|---|
| Shrinkage rate | 23°C | ISO 294-4 | 0.40to0.70 % |
| Water absorption rate | 23°C,24hr | ISO 62 | 0.20 % |
| melt mass-flow rate | 260°C/5.0kg | ISO 1133 | 25 g/10min |
| density | ISO 1183 | 1.13 g/cm³ |
| Thermal performance | Test Condition | Test Method | ROMIRA GERMANY/Romiloy® 1035 F |
|---|---|---|---|
| Linear coefficient of thermal expansion | MD：23到55°C | ISO 11359-2 | 8.5E-05 cm/cm/°C |
| vicat | ISO 306/B50 | 121 °C | |
| Heat distortion temperature | 1.8MPa,未退火，HDT | ISO 75-2/A | 100 °C |