Technical Data Sheet
| physical property | Test Condition | Test Method | Test Result |
|---|
| melt mass-flow rate | | ASTM D1238 | 7.0 g/10min |
| Shrinkage rate | | 内部方法 | 0.60-0.80 % |
| Water absorption rate | | ISO 62 | 0.35 % |
| Water absorption rate | | ISO 62 | 0.15 % |
| flammability | Test Condition | Test Method | Test Result |
|---|
| UL flame retardant rating | | UL 94 | V-0 |
| Burning wire flammability index | | IEC 60695-2-12 | 960 °C |
| Hot filament ignition temperature | | IEC 60695-2-13 | 850 °C |
| Hot filament ignition temperature | | IEC 60695-2-13 | 850 °C |
| Mechanical properties | Test Condition | Test Method | Test Result |
|---|
| --1 | | ASTM D638 | 2300 Mpa |
| yield | | ASTM D638 | 62.0 Mpa |
| Yield, 50.0mm span | | ASTM D790 | 95.0 Mpa |
| yield | | ISO 527-2/50 | 62.0 Mpa |
| fracture | | ASTM D638 | 65.0 Mpa |
| fracture | | ISO 527-2/50 | 58.0 Mpa |
| yield | | ASTM D638 | 6.0 % |
| yield | | ISO 527-2/50 | 6.0 % |
| fracture | | ASTM D638 | 80 % |
| fracture | | ISO 527-2/50 | 75 % |
| 50.0mm span | | ASTM D790 | 2160 Mpa |
| --7 | | ISO 178 | 2250 Mpa |
| --8 | | ISO 178 | 95.0 Mpa |
| Impact resistance | Test Condition | Test Method | Test Result |
|---|
| 23°C | | ASTM D256 | 400 J/m |
| 23°C | | ISO 180/1A | 40 kJ/m² |
| Dart impact | | ASTM D3763 | 70.0 J |
| Electrical performance | Test Condition | Test Method | Test Result |
|---|
| Compared to the Leakage Tracking Index (CTI) | | UL 746 | PLC 3 |
| High arc combustion index (HAI) | | UL 746 | PLC 1 |
| Hot wire ignition (HWI) | | UL 746 | PLC 3 |
| Thermal performance | Test Condition | Test Method | Test Result |
|---|
| 0.45MPa, Unanealed, 64.0mm span | | ISO 75-2/Bf | 135 °C |
| 1.8MPa, Unanealed, 3.20mm | | ASTM D648 | 123 °C |
| 1.8MPa, Unanealed, 64.0mm span | | ISO 75-2/Af | 123 °C |
| vicat | | ASTM D152513 | 140 °C |
| ball-indentation hardness | | IEC 60695-10-2 | Pass |
| Linear coefficient of thermal expansion | | ASTME831 | 6.8E-05 cm/cm/°C |
| Linear coefficient of thermal expansion | | ASTME831 | 6.7E-05 cm/cm/°C |
IMPORTANT NOTES: Plas.com collected the data in the data sheet from the material manufacturers. Plas.com makes the best effort to improve the accuracy of the data, but has no responsibility for the data. We strongly recommend verifying the validity of the data with the material manufacturers before making a final decision.