Material Comparison
Product Info
Product Name
Brand Name
Usages
Properties
Certificates
PC LUX9612-WH8E508X SABIC INNOVATIVE NANSHA
--
Lighting applications、Home appliance components、Automotive sector
optical performance 、UV resistance、Weather resistance、transparent、Flame retardant
--
--
--
--
--
--
--
--
--
--
--
--
--
--
--
Plastic Datasheets
| Impact resistance | Test Condition | Test Method | SABIC INNOVATIVE NANSHA/LUX9612-WH8E508X |
|---|---|---|---|
| 23°C | ISO 180/1A | 40 kJ/m² | |
| Dart impact | 23°C,TotalEnergy | ASTM D3763 | 70.0 J |
| 23°C | ASTM D256 | 400 J/m |
| Mechanical properties | Test Condition | Test Method | SABIC INNOVATIVE NANSHA/LUX9612-WH8E508X |
|---|---|---|---|
| yield | ASTM D638 | 62.0 Mpa | |
| ASTM D638 | 6.0 % | ||
| Yield, 50.0mm span | ASTM D790 | 95.0 Mpa | |
| yield | ISO 527-2/50 | 62.0 Mpa | |
| fracture | ISO 527-2/50 | 58.0 Mpa | |
| ASTM D638 | 65.0 Mpa | ||
| ISO 527-2/50 | 75 % | ||
| ASTM D638 | 80 % | ||
| yield | ISO 527-2/50 | 6.0 % | |
| --8 | ISO 178 | 95.0 Mpa | |
| 50.0mm span | ASTM D790 | 2160 Mpa | |
| --1 | ASTM D638 | 2300 Mpa | |
| --7 | ISO 178 | 2250 Mpa |
| Electrical performance | Test Condition | Test Method | SABIC INNOVATIVE NANSHA/LUX9612-WH8E508X |
|---|---|---|---|
| High arc combustion index (HAI) | HAI | UL 746 | PLC 1 |
| Hot wire ignition (HWI) | HWI | UL 746 | PLC 3 |
| Compared to the Leakage Tracking Index (CTI) | CTI | UL 746 | PLC 3 |
| flammability | Test Condition | Test Method | SABIC INNOVATIVE NANSHA/LUX9612-WH8E508X |
|---|---|---|---|
| Hot filament ignition temperature | 1.50mm | IEC 60695-2-13 | 850 °C |
| 1.00mm | IEC 60695-2-13 | 850 °C | |
| UL flame retardant rating | 1.50mm | UL 94 | V-0 |
| Burning wire flammability index | 1.00mm | IEC 60695-2-12 | 960 °C |
| physical property | Test Condition | Test Method | SABIC INNOVATIVE NANSHA/LUX9612-WH8E508X |
|---|---|---|---|
| Shrinkage rate | MD：3.20mm | 内部方法 | 0.60-0.80 % |
| Water absorption rate | 平衡,23°C,50%RH | ISO 62 | 0.15 % |
| 饱和,23°C | ISO 62 | 0.35 % | |
| melt mass-flow rate | 300°C/1.2kg | ASTM D1238 | 7.0 g/10min |
| Thermal performance | Test Condition | Test Method | SABIC INNOVATIVE NANSHA/LUX9612-WH8E508X |
|---|---|---|---|
| Linear coefficient of thermal expansion | TD:-40到40°C | ASTME831 | 6.7E-05 cm/cm/°C |
| 0.45MPa, Unanealed, 64.0mm span | ISO 75-2/Bf | 135 °C | |
| 1.8MPa, Unanealed, 64.0mm span | ISO 75-2/Af | 123 °C | |
| 1.8MPa, Unanealed, 3.20mm | ASTM D648 | 123 °C | |
| vicat | ASTM D152513 | 140 °C | |
| ball-indentation hardness | 125°C | IEC 60695-10-2 | Pass |
| Linear coefficient of thermal expansion | MD:-40到40°C | ASTME831 | 6.8E-05 cm/cm/°C |