PC PANLITE® ML-3110ZHP
26
- Properties:Thermal stabilitytransparent
- Usages:CastersFitness equipment
Compare
View PricesTechnical Data Sheet
| physical property | Test Condition | Test Method | Test Result |
|---|---|---|---|
| Dissolving fingers | ISO 1133 | 8 cm310min |
| optical performance | Test Condition | Test Method | Test Result |
|---|---|---|---|
| transmittance | JIS K7136 | 59 % | |
| dispersity | In-house method | 60 % |
| Mechanical properties | Test Condition | Test Method | Test Result |
|---|---|---|---|
| Yield tensile strength | ISO 527-1,2 | 61 Mpa | |
| Tensile strength at break | ISO 527-1 | 65 Mpa | |
| elongation at break | ISO 527-1 | 120 % | |
| Flexural modulus | ISO 178 | 2200 Mpa | |
| bending strength | ISO 178 | 95 Mpa | |
| Notch impact strength | ISO 179 | 20 kJ/m² | |
| Izod notch impact strength | ASTM D256/ISO 179 | 20 kg·cm/cm(J/M)ft·lb/in | |
| elongation at break | ASTM D638/ISO 527 | 66 % | |
| tensile strength | ASTM D638/ISO 527 | 61 kg/cm²(MPa)[Lb/in²] | |
| Flexural modulus | ASTM D790/ISO 178 | 2300 kg/cm²(MPa)[Lb/in²] | |
| bending strength | ASTM D790/ISO 178 | 96 kg/cm²(MPa)[Lb/in²] | |
| Tensile elongation at break (elongation at break) | ASTM D638/ISO 527 | 120 % |
| Physical properties | Test Condition | Test Method | Test Result |
|---|---|---|---|
| Mold Shrinkage | ASTM D955 | 0.5~0.7 % |
| Thermal performance | Test Condition | Test Method | Test Result |
|---|---|---|---|
| ISO 75-1,2 | 129 °C | ||
| UL94 | V-2 | ||
| ASTM D648/ISO 75 | 122 ℃（℉） | ||
| Linear expansion coefficient | ASTM D696/ISO 11359 | 0.7 mm/mm.℃ |
IMPORTANT NOTES: Plas.com collected the data in the data sheet from the material manufacturers. Plas.com makes the best effort to improve the accuracy of the data, but has no responsibility for the data. We strongly recommend verifying the validity of the data with the material manufacturers before making a final decision.