Material Comparison
Product Info
Product Name
Brand Name
Usages
Properties
Certificates
PC ML-3110ZHP TEIJIN JAPAN
PANLITE®
Casters、Fitness equipment
Thermal stability、transparent
--
--
--
--
--
--
--
--
--
--
--
--
--
--
--
Plastic Datasheets
| Mechanical properties | Test Condition | Test Method | TEIJIN JAPAN/ML-3110ZHP |
|---|---|---|---|
| bending strength | ASTM D790/ISO 178 | 96 kg/cm²(MPa)[Lb/in²] | |
| Flexural modulus | ASTM D790/ISO 178 | 2300 kg/cm²(MPa)[Lb/in²] | |
| elongation at break | 50mm/min | ISO 527-1 | 120 % |
| Izod notch impact strength | ASTM D256/ISO 179 | 20 kg·cm/cm(J/M)ft·lb/in | |
| Yield tensile strength | 50mm/min | ISO 527-1,2 | 61 Mpa |
| Tensile strength at break | 50mm/min | ISO 527-1 | 65 Mpa |
| Notch impact strength | Notched | ISO 179 | 20 kJ/m² |
| elongation at break | ASTM D638/ISO 527 | 66 % | |
| Tensile elongation at break (elongation at break) | ASTM D638/ISO 527 | 120 % | |
| tensile strength | ASTM D638/ISO 527 | 61 kg/cm²(MPa)[Lb/in²] | |
| bending strength | 2mm/min | ISO 178 | 95 Mpa |
| Flexural modulus | 2mm/min | ISO 178 | 2200 Mpa |
| optical performance | Test Condition | Test Method | TEIJIN JAPAN/ML-3110ZHP |
|---|---|---|---|
| transmittance | 1.5mmt | JIS K7136 | 59 % |
| dispersity | 2.0mmt | In-house method | 60 % |
| Physical properties | Test Condition | Test Method | TEIJIN JAPAN/ML-3110ZHP |
|---|---|---|---|
| Mold Shrinkage | ASTM D955 | 0.5~0.7 % |
| physical property | Test Condition | Test Method | TEIJIN JAPAN/ML-3110ZHP |
|---|---|---|---|
| Dissolving fingers | 300℃ | ISO 1133 | 8 cm310min |
| Thermal performance | Test Condition | Test Method | TEIJIN JAPAN/ML-3110ZHP |
|---|---|---|---|
| ASTM D648/ISO 75 | 122 ℃（℉） | ||
| 阻燃性，1.0mm/3.0mm | UL94 | V-2 | |
| 1.80MPa | ISO 75-1,2 | 129 °C | |
| Linear expansion coefficient | ASTM D696/ISO 11359 | 0.7 mm/mm.℃ |