| physical property | Test Condition | Test Method | Test Result |
|---|
| density | | ISO1183 | 1.05 g/cm³ |
| Shrinkage rate | | ISO294-4 | 1.2 % |
| Shrinkage rate | | ISO294-4 | 0.65 % |
| Water absorption rate | | ISO62 | 0.50 % |
| flammability | Test Condition | Test Method | Test Result |
|---|
| UL flame retardant rating | | UL94 | HB |
| UL flame retardant rating | | UL94 | HB |
| Supplementary Information | Test Condition | Test Method | Test Result |
|---|
| ISO Shortcut | | ISO1874 | PA12-P,EHL,22-002 |
| ElectrolyticalCorrosion | | IEC60426 | A1 |
| Impact resistance | Test Condition | Test Method | Test Result |
|---|
| Impact strength of simply supported beam without notch | | ISO179/1eU | NoBreak |
| Impact strength of simply supported beam without notch | | ISO179/1eU | NoBreak |
| Charpy Notched Impact Strength | | ISO179/1eA | 6.0 kJ/m² |
| Charpy Notched Impact Strength | | ISO179/1eA | NoBreak |
| Mechanical properties | Test Condition | Test Method | Test Result |
|---|
| Tensile modulus | | ISO527-2 | 230 MPa |
| Tensile stress | Yield | ISO527-2 | 18.0 MPa |
| Tensile strain | Yield | ISO527-2 | 45 % |
| Tensile strain | Break | ISO527-2 | >50 % |
| Electrical performance | Test Condition | Test Method | Test Result |
|---|
| Volume resistivity | | IEC60093 | 1E+10 ohms·cm |
| dielectric strength | | IEC60243-1 | 31 kV/mm |
| | IEC60250 | 17.0 |
| | IEC60250 | 3.80 |
| Dissipation Factor | | IEC60250 | 0.30 |
| Dissipation Factor | | IEC60250 | 0.24 |
| CTI | | IEC60112 | 600 V |
| CTI | | IEC60112 | >600 V |
| Thermal performance | Test Condition | Test Method | Test Result |
|---|
| | ISO75-2/B | 70.0 °C |
| | ISO75-2/A | 40.0 °C |
| vicat | | ISO306/A | 145 °C |
| vicat | | ISO306/B | 100 °C |
| melting temperature | | ISO11357-3 | 164 °C |
| | ISO11359-2 | 1.8E-04 cm/cm/°C |
IMPORTANT NOTES: Plas.com collected the data in the data sheet from the material manufacturers. Plas.com makes the best effort to improve the accuracy of the data, but has no responsibility for the data. We strongly recommend verifying the validity of the data with the material manufacturers before making a final decision.