TPO PRE-ELEC® PP 1370
0
CompareTechnical Data Sheet
| physical property | Test Condition | Test Method | Test Result |
|---|---|---|---|
| density | ASTM D792 | 0.969 g/cm³ | |
| ISO 1183 | 0.980 g/cm³ | ||
| melt mass-flow rate | ASTM D1238 | 2.0 g/10min | |
| ASTM D1238 | 12 g/10min | ||
| ISO 1133 | 2.0 g/10min | ||
| ISO 1133 | 12 g/10min | ||
| Shrinkage rate | ASTM D955 | 1.2to1.8 % | |
| ISO 294-4 | 1.2to1.8 % |
| hardness | Test Condition | Test Method | Test Result |
|---|---|---|---|
| Shore hardness | Shore A | ASTM D2240 | 96 |
| ASTM D2240 | 71 | ||
| Shore A | ISO 868 | 96 | |
| ISO 868 | 71 |
| Impact resistance | Test Condition | Test Method | Test Result |
|---|---|---|---|
| Impact strength of cantilever beam gap | ASTM D256 | 4.20 kJ/m² | |
| ASTM D256 | NoBreak | ||
| ISO 180 | 5.0 kJ/m² | ||
| ISO 180 | NoBreak | ||
| Suspended wall beam without notch impact strength | ASTM D256 | NoBreak | |
| ASTM D256 | NoBreak | ||
| ISO 180 | NoBreak | ||
| ISO 180 | NoBreak | ||
| Charpy Notched Impact Strength | ASTM D256 | 8.4 kJ/m² | |
| ISO 179 | 10 kJ/m² | ||
| ISO 179 | 24 kJ/m² | ||
| ASTM D256 | 23 kJ/m² | ||
| Impact strength of simply supported beam without notch | ASTM D256 | 61 kJ/m² | |
| ISO 179 | 60 kJ/m² | ||
| ISO 179 | NoBreak | ||
| ASTM D256 | NoBreak |
| Mechanical properties | Test Condition | Test Method | Test Result |
|---|---|---|---|
| tensile strength | ASTM D638 | 17.9 MPa | |
| Yield | ASTM D638 | 26.2 MPa | |
| Yield | ISO 527-2 | 26.0 MPa | |
| ISO 527-2 | 18.0 MPa | ||
| elongation | Yield | ASTM D638 | 10 % |
| Tensile strain | Yield | ISO 527-2 | 10 % |
| elongation | Break | ASTM D638 | 30 % |
| Tensile strain | ISO 527-2 | 30 % | |
| Flexural modulus | ASTM D790 | 1200 MPa | |
| ISO 178 | 1200 MPa |
| Electrical performance | Test Condition | Test Method | Test Result |
|---|---|---|---|
| Surface Resistivity | ESDSTM11.11 | <1.0E+4 ohms | |
| IEC 61340-2-3 | <1.0E+4 ohms | ||
| Volume resistivity | 内部方法 | <1.0E+3 ohms·cm |
| Thermal performance | Test Condition | Test Method | Test Result |
|---|---|---|---|
| Heat distortion temperature | ASTM D648B | 82.8 °C | |
| ISO 75-2/Bf | 83.0 °C | ||
| ASTM D648A | 53.9 °C | ||
| ISO 75-2/Af | 54.0 °C | ||
| vicat | ASTM D15253 | 149 °C | |
| ISO 306/A50 | 150 °C |
IMPORTANT NOTES: Plas.com collected the data in the data sheet from the material manufacturers. Plas.com makes the best effort to improve the accuracy of the data, but has no responsibility for the data. We strongly recommend verifying the validity of the data with the material manufacturers before making a final decision.