TPO PRE-ELEC® PP 1370 Premix Oy
--
--
--
--
--
--
--
--
--
--
--
--
--
--
--
--
--
--

Plastic Datasheets

Impact resistanceTest ConditionTest MethodPremix Oy/PRE-ELEC® PP 1370
Impact strength of cantilever beam gap23°C,4.00mm，AreaASTM D256NoBreak
Charpy Notched Impact Strength-20°CASTM D2568.4 kJ/m²
Impact strength of simply supported beam without notch-20°CASTM D25661 kJ/m²
Charpy Notched Impact Strength23°CASTM D25623 kJ/m²
Impact strength of cantilever beam gap-20°CISO 1805.0 kJ/m²
Suspended wall beam without notch impact strength-20°C,4.00mmASTM D256NoBreak
Impact strength of simply supported beam without notch23°CASTM D256NoBreak
Impact strength of cantilever beam gap23°CISO 180NoBreak
Charpy Notched Impact Strength23°CISO 17924 kJ/m²
Suspended wall beam without notch impact strength-20°CISO 180NoBreak
Impact strength of cantilever beam gap-20°C,4.00mm，AreaASTM D2564.20 kJ/m²
Impact strength of simply supported beam without notch23°CISO 179NoBreak
-20°CISO 17960 kJ/m²
Suspended wall beam without notch impact strength23°CISO 180NoBreak
Charpy Notched Impact Strength-20°CISO 17910 kJ/m²
Suspended wall beam without notch impact strength23°C,4.00mmASTM D256NoBreak
hardnessTest ConditionTest MethodPremix Oy/PRE-ELEC® PP 1370
Shore hardness邵氏DASTM D224071
邵氏DISO 86871
邵氏AISO 86896
邵氏AASTM D224096
Mechanical propertiesTest ConditionTest MethodPremix Oy/PRE-ELEC® PP 1370
elongation断裂ASTM D63830 %
tensile strength ASTM D63817.9 MPa
elongation屈服ASTM D63810 %
Tensile strain屈服ISO 527-210 %
断裂,4.00mmISO 527-230 %
Flexural modulus4.00mmASTM D7901200 MPa
4.00mmISO 1781200 MPa
tensile strength 屈服ASTM D63826.2 MPa
屈服ISO 527-226.0 MPa
4.00mmISO 527-218.0 MPa
Electrical performanceTest ConditionTest MethodPremix Oy/PRE-ELEC® PP 1370
Surface ResistivityESDSTM11.11<1.0E+4 ohms
IEC 61340-2-3<1.0E+4 ohms
Volume resistivity内部方法<1.0E+3 ohms·cm
physical property Test ConditionTest MethodPremix Oy/PRE-ELEC® PP 1370
melt mass-flow rate230°C/5.0kgASTM D123812 g/10min
Shrinkage rateMDASTM D9551.2to1.8 %
ISO 294-41.2to1.8 %
melt mass-flow rate230°C/2.16kgASTM D12382.0 g/10min
densityASTM D7920.969 g/cm³
ISO 11830.980 g/cm³
melt mass-flow rate230°C/5.0kgISO 113312 g/10min
230°C/2.16kgISO 11332.0 g/10min
Thermal performanceTest ConditionTest MethodPremix Oy/PRE-ELEC® PP 1370
Heat distortion temperature1.8MPa,未退火，HDTASTM D648A53.9 °C
1.8MPa,未退火，HDTISO 75-2/Af54.0 °C
vicatISO 306/A50150 °C
ASTM D15253149 °C
Heat distortion temperature0.45MPa,未退火，HDTASTM D648B82.8 °C
0.45MPa,未退火，HDTISO 75-2/Bf83.0 °C