Technical Data Sheet
| physical property | Test Condition | Test Method | Test Result |
|---|
| density | | ASTMD792 | 1.20 g/cm³ |
| melt mass-flow rate | | ASTMD1238 | 17 g/10min |
| Shrinkage rate | | ASTM D955 | 0.50to0.70 % |
| Water absorption rate | | ASTM D570 | 0.23 % |
| hardness | Test Condition | Test Method | Test Result |
|---|
| Rockwell hardness | M-Scale | ASTM D785 | 75 |
| Rockwell hardness | R-Scale | ASTM D785 | 120 |
| optical performance | Test Condition | Test Method | Test Result |
|---|
| refractive index | | ASTMD542 | 1.586 |
| transmissivity | | ASTM D1003 | 89.0 % |
| flammability | Test Condition | Test Method | Test Result |
|---|
| UL flame retardant rating | | UL 94 | HB |
| Hot filament ignition temperature | | IEC 60695-2-13 | 960 °C |
| Mechanical properties | Test Condition | Test Method | Test Result |
|---|
| tensile strength | Yield | ASTMD638 | 63.0 MPa |
| tensile strength | Break | ASTMD638 | 68.0 MPa |
| elongation | Break | ASTMD638 | 100 % |
| Flexural modulus | | ASTMD790 | 2350 MPa |
| bending strength | | ASTMD790 | 93.0 MPa |
| Tensile modulus | | ASTMD638 | 2300 MPa |
| Impact resistance | Test Condition | Test Method | Test Result |
|---|
| Impact strength of cantilever beam gap | | ASTM D256 | 780 J/m |
| Electrical performance | Test Condition | Test Method | Test Result |
|---|
| Dissipation Factor | | ASTM D150 | 9.2E-03 |
| arc resistance | | ASTM D495 | 110 sec |
| Volume resistivity | | ASTM D257 | 1E+16 ohms·cm |
| dielectric strength | | ASTM D149 | 29 kV/mm |
| dielectric constant | | ASTM D150 | 2.91 |
| dielectric constant | | ASTM D150 | 2.85 |
| Dissipation Factor | | ASTM D150 | 6.6E-04 |
| Thermal performance | Test Condition | Test Method | Test Result |
|---|
| Heat distortion temperature | | ASTMD648 | 132 °C |
| Linear coefficient of thermal expansion | | ASTM D696 | 6.5E-05 cm/cm/°C |
IMPORTANT NOTES: Plas.com collected the data in the data sheet from the material manufacturers. Plas.com makes the best effort to improve the accuracy of the data, but has no responsibility for the data. We strongly recommend verifying the validity of the data with the material manufacturers before making a final decision.