Technical Data Sheet
| physical property | Test Condition | Test Method | Test Result |
|---|
| density | | ASTMD792 | 1.29 g/cm³ |
| density | | ASTMD792 | 1.29 g/cm³ |
| flammability | Test Condition | Test Method | Test Result |
|---|
| burning rate | | UL94 | <16 mm/min |
| UL flame retardant rating | | UL94 | HB |
| burning rate | | UL94 | <16 mm/min |
| UL flame retardant rating | | UL94 | HB |
| Mechanical properties | Test Condition | Test Method | Test Result |
|---|
| Tensile modulus | | ASTMD638 | 2290 MPa |
| tensile strength | Break | ASTMD638 | 21.0 MPa |
| elongation | Break | ASTMD638 | 19 % |
| Tensile modulus | | ASTMD638 | 2290 MPa |
| tensile strength | Break | ASTMD638 | 21.0 MPa |
| elongation | Break | ASTMD638 | 19 % |
| Flexural modulus | | ASTMD790 | 2110 MPa |
| bending strength | | ASTMD790 | 33.0 MPa |
| Flexural modulus | | ASTMD790 | 2110 MPa |
| bending strength | | ASTMD790 | 33.0 MPa |
| Impact resistance | Test Condition | Test Method | Test Result |
|---|
| Impact strength of cantilever beam gap | | ASTMD256 | 79 J/m |
| Suspended wall beam without notch impact strength | | ASTMD256 | 370 J/m |
| Impact strength of cantilever beam gap | | ASTMD256 | 79 J/m |
| Suspended wall beam without notch impact strength | | ASTMD256 | 370 J/m |
| Electrical performance | Test Condition | Test Method | Test Result |
|---|
| Surface Resistivity | | ESDSTM11.11 | 52 ohms |
| Volume resistivity | | ASTMD257 | 16 ohms·cm |
| StaticDecay | | 内部方法 | 10 msec |
| Surface Resistance | | ESDSTM11.11 | 5.0 ohms |
| Surface Resistivity | | ESDSTM11.11 | 52 ohms |
| Volume resistivity | | ASTMD257 | 16 ohms·cm |
| StaticDecay | | 内部方法 | 10 msec |
| Surface Resistance | | ESDSTM11.11 | 5.0 ohms |
| Thermal performance | Test Condition | Test Method | Test Result |
|---|
| Heat distortion temperature | | ASTMD648 | 65.0 °C |
| Heat distortion temperature | | ASTMD648 | 65.0 °C |
IMPORTANT NOTES: Plas.com collected the data in the data sheet from the material manufacturers. Plas.com makes the best effort to improve the accuracy of the data, but has no responsibility for the data. We strongly recommend verifying the validity of the data with the material manufacturers before making a final decision.