Technical Data Sheet
| physical property | Test Condition | Test Method | Test Result |
|---|
| Specific volume | | ASTM D1475 | 0.863 cm³/g |
| Shrinkage rate | | ASTM D2566 | 0.50 % |
| Viscosity | | ASTM D2393 | Paste |
| density | | ASTM D1475 | 1.16 g/cm³ |
| thermosetting | Test Condition | Test Method | Test Result |
|---|
| stripping time | | | 90 min |
| STORAGE STABILITY | | ASTM D2471 | 8.0to10 min |
| hardness | Test Condition | Test Method | Test Result |
|---|
| Shore hardness | | ASTM D2240 | 70 |
| Supplementary Information | Test Condition | Test Method | Test Result |
|---|
| Mixing Ratio | | | 41A:100Bbyweight1A:3Bbyvolume |
| Mechanical properties | Test Condition | Test Method | Test Result |
|---|
| Tensile modulus | | ASTM D638 | 1160 MPa |
| tensile strength | Break | ASTM D638 | 11.0 MPa |
| elongation | Break | ASTM D638 | 1.5 % |
| Flexural modulus | | ASTM D790 | 1030 MPa |
| bending strength | | ASTM D790 | 23.5 MPa |
| Compression Modulus | | ASTM D695 | 336 MPa |
| compressive strength | | ASTM D695 | 23.6 MPa |
| Thermal performance | Test Condition | Test Method | Test Result |
|---|
| Heat distortion temperature | | ASTM D648 | 54.4 °C |
IMPORTANT NOTES: Plas.com collected the data in the data sheet from the material manufacturers. Plas.com makes the best effort to improve the accuracy of the data, but has no responsibility for the data. We strongly recommend verifying the validity of the data with the material manufacturers before making a final decision.