Technical Data Sheet
| physical property | Test Condition | Test Method | Test Result |
|---|
| MeltViscosity | | ASTM D3835 | 300 Pa·s |
| density | | | 1.30 g/cm³ |
| spiral flow length | | ASTM D3123 | 33.7 cm |
| Shrinkage rate | | | 1.1 % |
| Shrinkage rate | | | 1.3 % |
| Water absorption rate | Equilibrium | ASTM D570 | 0.060 % |
| hardness | Test Condition | Test Method | Test Result |
|---|
| Rockwell hardness | M-Scale | ASTM D785 | 98 |
| Shore hardness | | ASTM D2240 | 87 |
| flammability | Test Condition | Test Method | Test Result |
|---|
| UL flame retardant rating | | UL 94 | V-0 |
| Mechanical properties | Test Condition | Test Method | Test Result |
|---|
| elongation | | ASTM D638 | 20to25 % |
| Flexural modulus | | ASTM D790 | 4100 MPa |
| bending strength | | ASTM D790 | 185 MPa |
| compressive strength | | ASTM D695 | 135 MPa |
| Tensile modulus | | ASTM D638 | 4200 MPa |
| tensile strength | | ASTM D638 | 110 MPa |
| Impact resistance | Test Condition | Test Method | Test Result |
|---|
| Impact strength of cantilever beam gap | | ASTM D256 | 60 J/m |
| Impact strength of cantilever beam gap | | ASTM D256 | NoBreak |
| Thermal performance | Test Condition | Test Method | Test Result |
|---|
| Glass Transition Temperature | | ASTM D3418 | 152 °C |
| melting temperature | | ASTM D3418 | 372 °C |
| Heat distortion temperature | | ASTM D648 | 175 °C |
| Continuous use temperature | | UL 746B | 280 °C |
IMPORTANT NOTES: Plas.com collected the data in the data sheet from the material manufacturers. Plas.com makes the best effort to improve the accuracy of the data, but has no responsibility for the data. We strongly recommend verifying the validity of the data with the material manufacturers before making a final decision.