PEK G-PAEK™ 1100G Gharda Chemicals Ltd.
--
--
--
--
--
--
--
--
--
--
--
--
--
--
--
--
--
--
Plastic Datasheets
| Impact resistance | Test Condition | Test Method | Gharda Chemicals Ltd./G-PAEK™ 1100G |
|---|---|---|---|
| Impact strength of cantilever beam gap | 23°C | ASTM D256 | 60 J/m |
| ASTM D256 | NoBreak |
| hardness | Test Condition | Test Method | Gharda Chemicals Ltd./G-PAEK™ 1100G |
|---|---|---|---|
| Shore hardness | 邵氏D | ASTM D2240 | 87 |
| Rockwell hardness | M级 | ASTM D785 | 98 |
| Mechanical properties | Test Condition | Test Method | Gharda Chemicals Ltd./G-PAEK™ 1100G |
|---|---|---|---|
| bending strength | 23°C | ASTM D790 | 185 MPa |
| compressive strength | ASTM D695 | 135 MPa | |
| Tensile modulus | 23°C | ASTM D638 | 4200 MPa |
| Flexural modulus | 23°C | ASTM D790 | 4100 MPa |
| tensile strength | 屈服,23°C | ASTM D638 | 110 MPa |
| elongation | 断裂,23°C | ASTM D638 | 20to25 % |
| flammability | Test Condition | Test Method | Gharda Chemicals Ltd./G-PAEK™ 1100G |
|---|---|---|---|
| UL flame retardant rating | 0.8mm | UL 94 | V-0 |
| physical property | Test Condition | Test Method | Gharda Chemicals Ltd./G-PAEK™ 1100G |
|---|---|---|---|
| density | 1.30 g/cm³ | ||
| Shrinkage rate | MD3 | 1.1 % | |
| Water absorption rate | 平衡 | ASTM D570 | 0.060 % |
| MeltViscosity | 400°C,1000sec^-1 | ASTM D3835 | 300 Pa·s |
| spiral flow length | ASTM D3123 | 33.7 cm | |
| Shrinkage rate | TD3 | 1.3 % |
| Thermal performance | Test Condition | Test Method | Gharda Chemicals Ltd./G-PAEK™ 1100G |
|---|---|---|---|
| Heat distortion temperature | 1.8MPa,未退火，HDT | ASTM D648 | 175 °C |
| Continuous use temperature | UL 746B | 280 °C | |
| melting temperature | ASTM D3418 | 372 °C | |
| Glass Transition Temperature | ASTM D3418 | 152 °C |