Biodeg Polymers S 5630
0
CompareTechnical Data Sheet
| physical property | Test Condition | Test Method | Test Result |
|---|---|---|---|
| density | ISO 1183 | 1.55 g/cm³ | |
| Apparent density | ISO 60 | 0.90 g/cm³ | |
| melt mass-flow rate | ISO 1133 | 10to12 g/10min | |
| Melt volume flow rate | ISO 1133 | 8.00to10.0 cm³/10min |
| Mechanical properties | Test Condition | Test Method | Test Result |
|---|---|---|---|
| Tensile strain change rate | ISO 527 | 6.00 vol% | |
| Fracture bending strain | ISO 178 | NoBreak % | |
| Tensile modulus | ISO 527-2 | 2160 MPa | |
| tensile strength | Break | ISO 527-2 | 29.0 MPa |
| ISO 527 | 32.0 MPa | ||
| Tensile strain | Break | ISO 527-2 | 9.0 % |
| Flexural modulus | ISO 178 | 2400 MPa | |
| bending strength | ISO 178 | 46.0 MPa |
| Impact resistance | Test Condition | Test Method | Test Result |
|---|---|---|---|
| Charpy Notched Impact Strength | ISO 179/1eA | 3.0 kJ/m² | |
| Impact strength of simply supported beam without notch | ISO 179/1eU | 51 kJ/m² |
| Thermal performance | Test Condition | Test Method | Test Result |
|---|---|---|---|
| Heat distortion temperature | ISO 75-2/B | 68.0 °C | |
| vicat | ISO 306/A | 105 °C | |
| melting temperature | ISO 3146 | 140to160 °C |
IMPORTANT NOTES: Plas.com collected the data in the data sheet from the material manufacturers. Plas.com makes the best effort to improve the accuracy of the data, but has no responsibility for the data. We strongly recommend verifying the validity of the data with the material manufacturers before making a final decision.