Technical Data Sheet
| physical property | Test Condition | Test Method | Test Result |
|---|
| Shrinkage rate | | ASTM D995 | 0.776 % |
| Shrinkage rate | | ASTM D995 | 0.811 % |
| Shrinkage rate | | | 1.06 g/cm³ |
| Shrinkage rate | | | 2.17 % |
| Shrinkage rate | | | 15.1 g/10min |
| hardness | Test Condition | Test Method | Test Result |
|---|
| R | | | 99.2 R |
| Mechanical properties | Test Condition | Test Method | Test Result |
|---|
| tensile strength | | | 42.6 MPa |
| tensile strength | | | 39.8 MPa |
| Elastic modulus | | | 1830 MPa |
| bending strength | | | 67.5 MPa |
| Flexural modulus | | | 1840 MPa |
| elongation | Break | | 81.5 % |
| elongation | Break | | 8.94 % |
| Impact strength of cantilever beam gap | | | 634 J/m |
| Other performance | Test Condition | Test Method | Test Result |
|---|
| specific heat | | | 2.2E+03 J/Kg/°C |
| thermal conductivity | | | 0.145 W/m/K |
| vicat | | | 130 °C |
| dielectric strength | | | 30.1 KV/mm |
| Dissipation Factor | | | 0.0376 |
| Compared to the Leakage Tracking Index (CTI) | | | PLC 0 |
| Breakdown voltage strength | | | 39.5 J |
| Flame retardant performance | Test Condition | Test Method | Test Result |
|---|
| GWIT | | IEC 60695-2-12 | 650 °C |
| UL flame retardant rating | | UL -94 | HB - |
| Electrical performance | Test Condition | Test Method | Test Result |
|---|
| Volume resistivity | | | 6.9E+14 Ω.cm |
| Surface Resistivity | | | 1.32E+15 Ω.cm |
| dielectric constant | | | 3.66 |
IMPORTANT NOTES: Plas.com collected the data in the data sheet from the material manufacturers. Plas.com makes the best effort to improve the accuracy of the data, but has no responsibility for the data. We strongly recommend verifying the validity of the data with the material manufacturers before making a final decision.