Material Comparison
Product Info
Product Name
Brand Name
Usages
Properties
Certificates
ABS Resblend PA/ABS Polimarky Spolka Jawna
--
--
--
--
--
--
--
--
--
--
--
--
--
--
--
--
--
--
Plastic Datasheets
| Other performance | Test Condition | Test Method | Polimarky Spolka Jawna/Resblend PA/ABS |
|---|---|---|---|
| dielectric strength | 30.1 KV/mm | ||
| Breakdown voltage strength | 39.5 J | ||
| thermal conductivity | 0.145 W/m/K | ||
| Dissipation Factor | 0.0376 | ||
| specific heat | 2.2E+03 J/Kg/°C | ||
| Compared to the Leakage Tracking Index (CTI) | PLC 0 | ||
| vicat | 130 °C |
| hardness | Test Condition | Test Method | Polimarky Spolka Jawna/Resblend PA/ABS |
|---|---|---|---|
| R | 99.2 R |
| Mechanical properties | Test Condition | Test Method | Polimarky Spolka Jawna/Resblend PA/ABS |
|---|---|---|---|
| Impact strength of cantilever beam gap | 634 J/m | ||
| tensile strength | 39.8 MPa | ||
| Elastic modulus | 1830 MPa | ||
| bending strength | 67.5 MPa | ||
| Flexural modulus | 1840 MPa | ||
| elongation | 断裂 | 8.94 % |
| Electrical performance | Test Condition | Test Method | Polimarky Spolka Jawna/Resblend PA/ABS |
|---|---|---|---|
| Volume resistivity | 6.9E+14 Ω.cm | ||
| Surface Resistivity | 1.32E+15 Ω.cm | ||
| dielectric constant | 3.66 |
| Flame retardant performance | Test Condition | Test Method | Polimarky Spolka Jawna/Resblend PA/ABS |
|---|---|---|---|
| GWIT | IEC 60695-2-12 | 650 °C | |
| UL flame retardant rating | UL -94 | HB - |
| physical property | Test Condition | Test Method | Polimarky Spolka Jawna/Resblend PA/ABS |
|---|---|---|---|
| Shrinkage rate | 比重 | 1.06 g/cm³ | |
| MD | ASTM D995 | 0.776 % | |
| TD | ASTM D995 | 0.811 % | |
| 吸水率 | 2.17 % | ||
| 熔融流动指数 | 15.1 g/10min |