Technical Data Sheet
| physical property | Test Condition | Test Method | Test Result |
|---|
| Shrinkage rate | | ASTM D-955 | 0.3-0.5 % |
| density | | ISO 1183 | 1.61 g/cm³ |
| Water absorption rate | | ISO 62 | 0.09 % |
| processability | Test Condition | Test Method | Test Result |
|---|
| Shrinkage rate | | ISO 294-4 | 0.5-0.9 % |
| | | -- CM |
| Mechanical properties | Test Condition | Test Method | Test Result |
|---|
| Flexural modulus | | ASTM D-790 | 5000 Mpa |
| Charpy impact strength | | ASTM D-256 | 25 kJ/m² |
| Charpy impact strength | | ASTM D-256 | 7 kJ/m² |
| bending strength | | ASTM D-790 | 105 Mpa |
| Rockwell hardness | | ASTM D-785 | 90 M Scale |
| elongation | | ASTM D-638 | 3.4 % |
| Cantilever beam impact strength (notch) | | ASTM D-256 | 50 J/m |
| tensile strength | | ASTM D-638 | 80 Mpa |
| tensile strength | | ISO 527 | 115 Mpa |
| elongation | | ISO 527 | 3.8 % |
| bending strength | | ISO 178 | 185 Mpa |
| Flexural modulus | | ISO 178 | 7*103 Mpa |
| Charpy impact strength | | ISO 179（leA） | 9 kJ/m² |
| Flame retardant performance | Test Condition | Test Method | Test Result |
|---|
| Flame retardancy | | UL94 | V-0（0.8mm） |
| Electrical performance | Test Condition | Test Method | Test Result |
|---|
| | ASTM D-257 | 1014 Ω.cm |
| dielectric constant | | ASTM D-150 | 3.0 106Hz |
| Loss factor | | ASTM D-150 | 2.0×10-2 106Hz |
| dielectric strength | | ASTM D-149 | 23 MV/m |
| Betweenness constant | | IEC 60250 | 3.4 |
| dielectric loss tangent | | IEC 60250 | 1.8*10-2 |
| | IEC 60093 | 1*1014 Ω。m |
| dielectric strength | | IEC 60243 | 31 KV/m |
| | IEC 61621 | -- sec |
| CTI | | IEC 60112 | 250 V |
| ash content | | | 30 % |
| Thermal performance | Test Condition | Test Method | Test Result |
|---|
| Flame retardancy | | UL 94 | V-0 HB |
| | ASTM D-696 | 2.2 10-5℃mm/mm/℃ |
| | ASTM D-648 | 170 °C |
| | ISO 75f | 195 °C |
IMPORTANT NOTES: Plas.com collected the data in the data sheet from the material manufacturers. Plas.com makes the best effort to improve the accuracy of the data, but has no responsibility for the data. We strongly recommend verifying the validity of the data with the material manufacturers before making a final decision.