Technical Data Sheet
| physical property | Test Condition | Test Method | Test Result |
|---|
| density | | ASTM D792 | 1.10 g/cm³ |
| density | | ASTM D792 | 1.11 g/cm³ |
| Shrinkage rate | | ASTM D955 | 1.6to1.8 % |
| Shrinkage rate | | 内部方法 | 1.1to1.3 % |
| Shrinkage rate | | 内部方法 | 1.0to1.2 % |
| Water absorption rate | | ASTM D570 | 0.50 % |
| Water absorption rate | | ASTM D570 | 1.0 % |
| hardness | Test Condition | Test Method | Test Result |
|---|
| Rockwell hardness | R-Scale | ASTM D785 | 116 |
| flammability | Test Condition | Test Method | Test Result |
|---|
| UL flame retardant rating | | UL 94 | HB |
| Mechanical properties | Test Condition | Test Method | Test Result |
|---|
| elongation | Break | ASTM D638 | 60 % |
| Flexural modulus | | ASTM D790 | 2250 MPa |
| bending strength | | ASTM D790 | 95.8 MPa |
| tensile strength | Break | ASTM D638 | 55.2 MPa |
| tensile strength | Yield | ASTM D638 | 59.3 MPa |
| Impact resistance | Test Condition | Test Method | Test Result |
|---|
| Impact strength of cantilever beam gap | | ASTM D256 | 130 J/m |
| Impact strength of cantilever beam gap | | ASTM D256 | 240 J/m |
| Dart impact | | ASTM D3763 | 39.5 J |
| Dart impact | | ASTM D3763 | 50.8 J |
| Electrical performance | Test Condition | Test Method | Test Result |
|---|
| arc resistance | | ASTM D495 | PLC7 |
| Hot wire ignition (HWI) | | UL 746 | PLC 3 |
| Compared to the Leakage Tracking Index (CTI) | | UL 746 | PLC 1 |
| High arc combustion index (HAI) | | UL 746 | PLC 0 |
| High Voltage Arc Traceability Rate (HVTR) | | UL 746 | PLC 4 |
| Thermal performance | Test Condition | Test Method | Test Result |
|---|
| Linear coefficient of thermal expansion | | ASTME831 | 9E-05 cm/cm/°C |
| Linear coefficient of thermal expansion | | ASTME831 | 1.3E-04 cm/cm/°C |
| Linear coefficient of thermal expansion | | ASTME831 | 9E-05 cm/cm/°C |
| Linear coefficient of thermal expansion | | ASTME831 | 1.3E-04 cm/cm/°C |
| RTI Elec | | UL 746 | 50.0 °C |
| RTI Imp | | UL 746 | 50.0 °C |
| RTI | | UL 746 | 50.0 °C |
| Heat distortion temperature | | ASTM D648 | 193 °C |
| Heat distortion temperature | | ASTM D648 | 143 °C |
| vicat | | ASTM D15255 | 232 °C |
IMPORTANT NOTES: Plas.com collected the data in the data sheet from the material manufacturers. Plas.com makes the best effort to improve the accuracy of the data, but has no responsibility for the data. We strongly recommend verifying the validity of the data with the material manufacturers before making a final decision.