Material Comparison
Product Info
Product Name
Brand Name
Usages
Properties
Certificates
PS NORYL GTX™ GTX910 resin SABIC
--
--
--
--
--
--
--
--
--
--
--
--
--
--
--
--
--
--
Plastic Datasheets
| Impact resistance | Test Condition | Test Method | SABIC/NORYL GTX™ GTX910 resin |
|---|---|---|---|
| Impact strength of cantilever beam gap | -30°C | ASTM D256 | 130 J/m |
| 23°C | ASTM D256 | 240 J/m | |
| Dart impact | -30°C,EnergyatPeakLoad | ASTM D3763 | 39.5 J |
| 23°C,EnergyatPeakLoad | ASTM D3763 | 50.8 J |
| hardness | Test Condition | Test Method | SABIC/NORYL GTX™ GTX910 resin |
|---|---|---|---|
| Rockwell hardness | R级 | ASTM D785 | 116 |
| Mechanical properties | Test Condition | Test Method | SABIC/NORYL GTX™ GTX910 resin |
|---|---|---|---|
| elongation | 断裂 | ASTM D638 | 60 % |
| bending strength | 屈服,100mm跨距 | ASTM D790 | 95.8 MPa |
| tensile strength | 断裂 | ASTM D638 | 55.2 MPa |
| 屈服 | ASTM D638 | 59.3 MPa | |
| Flexural modulus | 100mm跨距 | ASTM D790 | 2250 MPa |
| Electrical performance | Test Condition | Test Method | SABIC/NORYL GTX™ GTX910 resin |
|---|---|---|---|
| High Voltage Arc Traceability Rate (HVTR) | HVTR | UL 746 | PLC 4 |
| High arc combustion index (HAI) | HAI | UL 746 | PLC 0 |
| Hot wire ignition (HWI) | HWI | UL 746 | PLC 3 |
| arc resistance | ASTM D495 | PLC7 | |
| Compared to the Leakage Tracking Index (CTI) | CTI | UL 746 | PLC 1 |
| flammability | Test Condition | Test Method | SABIC/NORYL GTX™ GTX910 resin |
|---|---|---|---|
| UL flame retardant rating | 1.5mm | UL 94 | HB |
| physical property | Test Condition | Test Method | SABIC/NORYL GTX™ GTX910 resin |
|---|---|---|---|
| Shrinkage rate | MD:130°C,1小时 | ASTM D955 | 1.6to1.8 % |
| Water absorption rate | 24hr,50%RH | ASTM D570 | 0.50 % |
| Shrinkage rate | MD:3.20mm | 内部方法 | 1.1to1.3 % |
| Water absorption rate | 平衡,50%RH | ASTM D570 | 1.0 % |
| density | -- | ASTM D792 | 1.11 g/cm³ |
| Shrinkage rate | TD:3.20mm | 内部方法 | 1.0to1.2 % |
| Thermal performance | Test Condition | Test Method | SABIC/NORYL GTX™ GTX910 resin |
|---|---|---|---|
| Linear coefficient of thermal expansion | TD:-40到95°C | ASTME831 | 9E-05 cm/cm/°C |
| Heat distortion temperature | 1.8MPa,未退火,6.40mm，HDT | ASTM D648 | 143 °C |
| Linear coefficient of thermal expansion | MD:60到138°C | ASTME831 | 1.3E-04 cm/cm/°C |
| vicat | ASTM D15255 | 232 °C | |
| Linear coefficient of thermal expansion | MD:-40到95°C | ASTME831 | 9E-05 cm/cm/°C |
| RTI Imp | UL 746 | 50.0 °C | |
| Heat distortion temperature | 0.45MPa,未退火,6.40mm，HDT | ASTM D648 | 193 °C |
| RTI | UL 746 | 50.0 °C | |
| Linear coefficient of thermal expansion | TD:60到138°C | ASTME831 | 1.3E-04 cm/cm/°C |
| RTI Elec | UL 746 | 50.0 °C |