Technical Data Sheet
| physical property | Test Condition | Test Method | Test Result |
|---|
| density | | ISO 1183 | 1.30 g/cm³ |
| Melt volume flow rate | | ISO 1133 | 14.0 cm3/10min |
| Shrinkage rate | | 内部方法 | 0.50-0.90 % |
| Water absorption rate | | ISO 62 | 0.50 % |
| Water absorption rate | | ISO 62 | 0.15 % |
| hardness | Test Condition | Test Method | Test Result |
|---|
| Rockwell hardness | | ISO 2039-2 | 113 |
| ball-indentation hardness | | ISO 2039-1 | 105 Mpa |
| flammability | Test Condition | Test Method | Test Result |
|---|
| UL flame retardant rating | | UL 94 | HB |
| Mechanical properties | Test Condition | Test Method | Test Result |
|---|
| Tensile modulus | | ISO 527-2/1 | 4500 Mpa |
| tensile strength | | ISO 527-2/5 | 90.0 Mpa |
| Tensile strain | | ISO 527-2/5 | 3.0 % |
| Flexural modulus | | ISO 178 | 4000 Mpa |
| bending strength | | ISO 178 | 140 Mpa |
| Impact resistance | Test Condition | Test Method | Test Result |
|---|
| Suspended wall beam without notch impact strength | | ISO 180/1U | 30 kJ/m² |
| Charpy Notched Impact Strength | | ISO 179/1eA | 3.5 kJ/m² |
| Charpy Notched Impact Strength | | ISO 179/1eA | 4.0 kJ/m² |
| Impact strength of simply supported beam without notch | | ISO 179/1eU | 35 kJ/m² |
| Impact strength of simply supported beam without notch | | ISO 179/1eU | 35 kJ/m² |
| Impact strength of cantilever beam gap | | ISO 180/1A | 3.0 kJ/m² |
| Impact strength of cantilever beam gap | | ISO 180/1A | 3.0 kJ/m² |
| Impact strength of cantilever beam gap | | ISO 180/1A | 3.0 kJ/m² |
| Suspended wall beam without notch impact strength | | ISO 180/1U | 30 kJ/m² |
| Electrical performance | Test Condition | Test Method | Test Result |
|---|
| Volume resistivity | | IEC 60093 | >1.0E+14 ohms·cm |
| dielectric strength | | IEC 60243-1 | 17 KV/mm |
| relative permittivity | | IEC 60250 | 3.30 |
| relative permittivity | | IEC 60250 | 3.30 |
| relative permittivity | | IEC 60250 | 3.10 |
| Dissipation Factor | | IEC 60250 | 2E-03 |
| Dissipation Factor | | IEC 60250 | 2E-03 |
| Dissipation Factor | | IEC 60250 | 0.020 |
| Surface Resistivity | | IEC 60093 | >1.0E+15 ohms |
| Thermal performance | Test Condition | Test Method | Test Result |
|---|
| 0.45MPa, Unanealed, 100mm span | | ISO 75-2/Be | 115 °C |
| 1.8MPa, Unanealed, 100mm span | | ISO 75-2/Ae | 105 °C |
| ball-indentation hardness | | IEC 60695-10-2 | Pass |
| Linear coefficient of thermal expansion | | ISO 11359-2 | 4E-05 cm/cm/°C |
| Linear coefficient of thermal expansion | | ISO 11359-2 | 1.1E-04 cm/cm/°C |
| thermal conductivity | | ISO 8302 | 0.19 W/m/K |
IMPORTANT NOTES: Plas.com collected the data in the data sheet from the material manufacturers. Plas.com makes the best effort to improve the accuracy of the data, but has no responsibility for the data. We strongly recommend verifying the validity of the data with the material manufacturers before making a final decision.