Material Comparison
Product Info
Product Name
Brand Name
Usages
Properties
Certificates
PC/PBT 1760T SABIC INNOVATIVE US
XENOY™
Automotive External Parts、Phone case、Shell
Chemical resistance、High mobility、Glass fiber reinforced、High impact resistance、Filler: Glass fiber reinf、11% filler by weight
--
--
--
--
--
--
--
--
--
--
--
--
--
--
--
Plastic Datasheets
| Thermal Properties | Test Condition | Test Method | SABIC INNOVATIVE US/1760T |
|---|---|---|---|
| Linear thermal expansion coefficient | TD:23到80°C | ISO11359-2 | 1.1E-04 cm/cm/°C |
| Thermal Conductivity | ISO8302 | 0.19 W/m/K | |
| Ball PressureTest | 75°C | IEC60695-10-2 | Pass |
| Linear thermal expansion coefficient | MD:23到80°C | ISO11359-2 | 4E-05 cm/cm/°C |
| 0.45MPa, Unannealed,100mm Span | ISO75-2/Be | 115 °C | |
| 1.8MPa, Unannealed,100mm Span | ISO75-2/Ae | 105 °C |
| Hardness | Test Condition | Test Method | SABIC INNOVATIVE US/1760T |
|---|---|---|---|
| Ball Indentation Hardness | H358/30 | ISO2039-1 | 105 Mpa |
| Rockwell Hardness | R计秤 | ISO2039-2 | 113 |
| Physical | Test Condition | Test Method | SABIC INNOVATIVE US/1760T |
|---|---|---|---|
| Density / Specific Gravity | ISO1183 | 1.30 g/cm³ | |
| Moisture Absorption | 平衡,23°C,50%RH | ISO62 | 0.15 % |
| Melt Volume flow Rate | 250°C/5.0kg | ISO1133 | 14.0 cm3/10min |
| Modeling Shrinkage | MD1 | 内部方法 | 0.50到0.90 % |
| Moisture Absorption | 饱和,23°C | ISO62 | 0.50 % |
| Mechanical Properties | Test Condition | Test Method | SABIC INNOVATIVE US/1760T |
|---|---|---|---|
| Flexural Modulus | ISO178 | 4000 Mpa | |
| Tensile Strain | 断裂 | ISO527-2/5 | 3.0 % |
| Tensile Modulus | ISO527-2/1 | 4500 Mpa | |
| Flexural Stress | ISO178 | 140 Mpa | |
| Tensile Stress | 断裂 | ISO527-2/5 | 90.0 Mpa |
| Impact Properties | Test Condition | Test Method | SABIC INNOVATIVE US/1760T |
|---|---|---|---|
| Notched Izod Impact Strength | -30°C | ISO180/1A | 3.0 kJ/m² |
| Charpy Unnotched Impact Strength | 23°C | ISO179/1eU | 35 kJ/m² |
| Unnotched Izod Impact Strength | 23°C | ISO180/1U | 30 kJ/m² |
| Charpy Notched Impact Strength | -30°C | ISO179/1eA | 3.5 kJ/m² |
| Notched Izod Impact Strength | 0°C | ISO180/1A | 3.0 kJ/m² |
| Charpy Notched Impact Strength | 23°C | ISO179/1eA | 4.0 kJ/m² |
| Unnotched Izod Impact Strength | -30°C | ISO180/1U | 30 kJ/m² |
| Charpy Unnotched Impact Strength | -30°C | ISO179/1eU | 35 kJ/m² |
| Notched Izod Impact Strength | 23°C | ISO180/1A | 3.0 kJ/m² |
| Flammability | Test Condition | Test Method | SABIC INNOVATIVE US/1760T |
|---|---|---|---|
| Flame Rating | 1.50mm,TestingbySABIC | UL94 | HB |
| Electrical Properties | Test Condition | Test Method | SABIC INNOVATIVE US/1760T |
|---|---|---|---|
| Dielectric Strength | 3.20mm,在油中 | IEC60243-1 | 17 KV/mm |
| Dissipation Factor? | 1MHz | IEC60250 | 0.020 |
| Volume Resistivity | IEC60093 | >1.0E+14 ohms·cm | |
| Relative Permittivity | 50Hz | IEC60250 | 3.30 |
| Dissipation Factor? | 60Hz | IEC60250 | 2E-03 |
| Relative Permittivity | 1MHz | IEC60250 | 3.10 |
| Dissipation Factor? | 50Hz | IEC60250 | 2E-03 |
| Surface Resistivity | IEC60093 | >1.0E+15 ohms | |
| Relative Permittivity | 60Hz | IEC60250 | 3.30 |