Technical Data Sheet
| physical property | Test Condition | Test Method | Test Result |
|---|
| Water absorption rate | | ISO 62 | 0.20 % |
| Shrinkage rate | | ASTM D955 | 0.50to1.0 % |
| Shrinkage rate | | ASTM D955 | 0.40to0.80 % |
| melt mass-flow rate | | ASTM D1238 | 2.0 g/10min |
| density | | ASTM D792 | 1.04 g/cm³ |
| hardness | Test Condition | Test Method | Test Result |
|---|
| Rockwell hardness | R-Scale | ASTM D785 | 105 |
| flammability | Test Condition | Test Method | Test Result |
|---|
| Hot filament ignition temperature | | IEC 60695-2-13 | 650 °C |
| UL flame retardant rating | | UL 94 | HB |
| UL flame retardant rating | | UL 94 | HB |
| Mechanical properties | Test Condition | Test Method | Test Result |
|---|
| Flexural modulus | | ASTM D790 | 4200 MPa |
| elongation | Break | ASTM D638 | 5.0 % |
| tensile strength | Break | ASTM D638 | 60.0 MPa |
| bending strength | Break | ASTM D790 | 80.0 MPa |
| Impact resistance | Test Condition | Test Method | Test Result |
|---|
| Impact strength of cantilever beam gap | | ASTM D256 | 60 J/m |
| Impact strength of cantilever beam gap | | ASTM D256 | 40 J/m |
| Electrical performance | Test Condition | Test Method | Test Result |
|---|
| Dissipation Factor | | IEC 60250 | 0.0 |
| relative permittivity | | IEC 60250 | 2.70 |
| dielectric strength | | IEC 60243-1 | 60 kV/mm |
| Volume resistivity | | IEC 60093 | 1E+15 ohms·cm |
| Surface Resistivity | | IEC 60093 | 1E+14 ohms |
| Thermal performance | Test Condition | Test Method | Test Result |
|---|
| Linear coefficient of thermal expansion | | ISO 11359-2 | 4E-05 cm/cm/°C |
| vicat | | ASTM D15254 | 125 °C |
| Heat distortion temperature | | ASTM D648 | 144 °C |
IMPORTANT NOTES: Plas.com collected the data in the data sheet from the material manufacturers. Plas.com makes the best effort to improve the accuracy of the data, but has no responsibility for the data. We strongly recommend verifying the validity of the data with the material manufacturers before making a final decision.