Technical Data Sheet
| physical property | Test Condition | Test Method | Test Result |
|---|
| melt mass-flow rate | | ASTM D1238 | 20 g/10min |
| Shrinkage rate | | ASTM D955 | 1.3 % |
| Water absorption rate | | ASTM D570 | 0.36 % |
| hardness | Test Condition | Test Method | Test Result |
|---|
| Shore hardness | | JISK6301 | 98 |
| Shore hardness | | ASTM D2240 | 57 |
| flammability | Test Condition | Test Method | Test Result |
|---|
| UL flame retardant rating | | UL 94 | HB |
| Supplementary Information | Test Condition | Test Method | Test Result |
|---|
| Resilience | | JISK6301 | 59.0 |
| Mechanical properties | Test Condition | Test Method | Test Result |
|---|
| compressive strength | | ASTM D695 | 19.1 Mpa |
| Taber abraser | | ASTM D1044 | 10.0 mg |
| tensile strength | | ASTM D638 | 38.0 Mpa |
| tensile strength | | ASTM D638 | 19.6 Mpa |
| elongation | | ASTM D638 | 500 % |
| Flexural modulus | | ASTM D790 | 289 Mpa |
| elastomer | Test Condition | Test Method | Test Result |
|---|
| tear strength | | ASTM D624 | 176 kN/m |
| compression set | | JISK6301 | 60 % |
| Electrical performance | Test Condition | Test Method | Test Result |
|---|
| Volume resistivity | | ASTM D257 | 2E+14 ohms·cm |
| dielectric strength | | JISK2111 | 30 KV/mm |
| Thermal performance | Test Condition | Test Method | Test Result |
|---|
| Heat distortion temperature | | ASTM D648 | 117 °C |
| brittle temperature | | JISK6301 | <-65.0 °C |
| vicat | | ASTM D1525 | 190 °C |
| melting temperature | | DSC | 212 °C |
| Linear coefficient of thermal expansion | | ASTME831 | 1.4E-04 cm/cm/°C |
IMPORTANT NOTES: Plas.com collected the data in the data sheet from the material manufacturers. Plas.com makes the best effort to improve the accuracy of the data, but has no responsibility for the data. We strongly recommend verifying the validity of the data with the material manufacturers before making a final decision.