Technical Data Sheet
| physical property | Test Condition | Test Method | Test Result |
|---|
| Shrinkage rate | | ASTM D955 | 0.40 % |
| Water absorption rate | | ASTM D570 | 0.70 % |
| Water absorption rate | Saturation | ASTM D570 | 3.2 % |
| density | | ASTM D792 | 1.46 g/cm³ |
| hardness | Test Condition | Test Method | Test Result |
|---|
| Rockwell hardness | R-Scale | ASTM D785 | 120 |
| Impact resistance | Test Condition | Test Method | Test Result |
|---|
| Suspended wall beam without notch impact strength | | ASTM D256 | 960 J/m |
| Impact strength of cantilever beam gap | | ASTM D256 | 130 J/m |
| Mechanical properties | Test Condition | Test Method | Test Result |
|---|
| shear strength | | ASTM D732 | 82.7 MPa |
| tensile strength | Yield | ASTM D638 | 217 MPa |
| elongation | Yield | ASTM D638 | 2.0 % |
| Flexural modulus | | ASTM D790 | 11400 MPa |
| bending strength | Yield | ASTM D790 | 283 MPa |
| compressive strength | | ASTM D695 | 165 MPa |
| Electrical performance | Test Condition | Test Method | Test Result |
|---|
| dielectric constant | | ASTM D150 | 3.85 |
| dielectric constant | | ASTM D150 | 0.00800 |
| Dissipation Factor | | ASTM D150 | 0.012 |
| Dissipation Factor | | ASTM D150 | 0.015 |
| Dissipation Factor | | ASTM D150 | 0.019 |
| Volume resistivity | | ASTM D257 | 1E+14 ohms·cm |
| dielectric strength | | ASTM D149 | 20 kV/mm |
| dielectric constant | | ASTM D150 | 4.30 |
| Thermal performance | Test Condition | Test Method | Test Result |
|---|
| Hot deformation temperature (HDT) | | ASTM D648 | 260 °C |
| Hot deformation temperature (HDT) | | ASTM D648 | 254 °C |
| | ASTM D696 | 2.7E-05 cm/cm/°C |
IMPORTANT NOTES: Plas.com collected the data in the data sheet from the material manufacturers. Plas.com makes the best effort to improve the accuracy of the data, but has no responsibility for the data. We strongly recommend verifying the validity of the data with the material manufacturers before making a final decision.
Compare