PA66 Modified Plastics MN 6/6-FG 40 美国Modified Plastics
--
--
填料,玻璃纤维增强材料,40%,填料按重量,
--
--
--
--
--
--
--
--
--
--
--
--
--
--
--

Plastic Datasheets

Impact resistanceTest ConditionTest Method美国Modified Plastics/Modified Plastics MN 6/6-FG 40
Impact strength of cantilever beam gap23°C,6.35mmASTM D256130 J/m
Suspended wall beam without notch impact strength23°C,6.35mmASTM D256960 J/m
hardnessTest ConditionTest Method美国Modified Plastics/Modified Plastics MN 6/6-FG 40
Rockwell hardnessR级ASTM D785120
Mechanical propertiesTest ConditionTest Method美国Modified Plastics/Modified Plastics MN 6/6-FG 40
elongation屈服ASTM D6382.0 %
bending strength屈服ASTM D790283 MPa
compressive strengthASTM D695165 MPa
Flexural modulusASTM D79011400 MPa
tensile strength 屈服ASTM D638217 MPa
shear strengthASTM D73282.7 MPa
Electrical performanceTest ConditionTest Method美国Modified Plastics/Modified Plastics MN 6/6-FG 40
Dissipation Factor1kHzASTM D1500.015
100HzASTM D1500.012
Volume resistivityASTM D2571E+14 ohms·cm
dielectric strengthASTM D14920 kV/mm
dielectric constant1kHzASTM D1503.85
Dissipation Factor1MHzASTM D1500.019
dielectric constant1MHzASTM D1500.00800
100HzASTM D1504.30
physical property Test ConditionTest Method美国Modified Plastics/Modified Plastics MN 6/6-FG 40
Shrinkage rateMDASTM D9550.40 %
Water absorption rate饱和ASTM D5703.2 %
24hrASTM D5700.70 %
densityASTM D7921.46 g/cm³
Thermal performanceTest ConditionTest Method美国Modified Plastics/Modified Plastics MN 6/6-FG 40
MDASTM D6962.7E-05 cm/cm/°C
Hot deformation temperature (HDT)1.8MPa,未退火，HDTASTM D648254 °C
0.45MPa,未退火，HDTASTM D648260 °C